Language selection

Search

Patent 2125152 Summary

Third-party information liability

Some of the information on this Web page has been provided by external sources. The Government of Canada is not responsible for the accuracy, reliability or currency of the information supplied by external sources. Users wishing to rely upon this information should consult directly with the source of the information. Content provided by external sources is not subject to official languages, privacy and accessibility requirements.

Claims and Abstract availability

Any discrepancies in the text and image of the Claims and Abstract are due to differing posting times. Text of the Claims and Abstract are posted:

  • At the time the application is open to public inspection;
  • At the time of issue of the patent (grant).
(12) Patent Application: (11) CA 2125152
(54) English Title: PROCESS FOR PRODUCING CAST AND SET PIECES OF JEWELLERY
(54) French Title: PROCEDE POUR LA FABRICATION DE BIJOUX MOULES AVEC PIERRES MONTEES
Status: Deemed Abandoned and Beyond the Period of Reinstatement - Pending Response to Notice of Disregarded Communication
Bibliographic Data
(51) International Patent Classification (IPC):
  • B22D 25/02 (2006.01)
  • A44C 17/04 (2006.01)
(72) Inventors :
  • MULLER, MANFRED (Germany)
(73) Owners :
  • MANFRED MULLER
(71) Applicants :
(74) Agent: MARKS & CLERK
(74) Associate agent:
(45) Issued:
(86) PCT Filing Date: 1992-12-03
(87) Open to Public Inspection: 1993-06-10
Examination requested: 1994-10-06
Availability of licence: N/A
Dedicated to the Public: N/A
(25) Language of filing: English

Patent Cooperation Treaty (PCT): Yes
(86) PCT Filing Number: PCT/EP1992/002792
(87) International Publication Number: WO 1993010686
(85) National Entry: 1994-06-03

(30) Application Priority Data:
Application No. Country/Territory Date
P 41 40 121.2 (Germany) 1991-12-05

Abstracts

English Abstract


ABSTRACT OF THE DISCLOSURE
In order to produce pieces of jewellery with one or
several set stones, a master pattern with settings for the
stones is produced, a master mould is produced by moulding
from the master pattern, a model is produced in the master
mould with a castable or injection mouldable modelling mass
that can be ejected by heating from the master mould, the
stones are inserted into the model and set by deformation of
the setting, a casting mould is produced be embedding the
model in a fire-resistant moulding mass and by ejecting the
modelling mass from the casting mould, metal is cast into the
casting mould by a spin casting or vacuum moulding process
and the piece of jewellery is removed from the mould once the
metal has cooled down.


Claims

Note: Claims are shown in the official language in which they were submitted.


Claims:
1. A process of making pieces of jewellery compris-
ing one or more set jewels, wherein
- a master pattern having empty settings for the jewels is
made;
- the master pattern containing no jewels is used to make a
master mold;
- a pattern is made in the master mold from a wax which can
be cast or injection-molded and can be expelled by being
heated as a pattern-making composition;
- the jewels are inserted into the settings of the pattern;
- the setting of the pattern is plastically deformed to fix
each jewel in its setting,
- a casting mold is made in that the pattern which does not
yet contain jewels is embedded in a refractory molding
composition and the pattern-making composition is ex-
pelled from the casting mold;
- metal is poured into the casting mold;
- the piece of jewellery is taken from the mold when the
metal has solidified,
- the jewels are inserted only into the pattern which has
been made by means of the master mold and are set in that
the settings are deformed.
2. A process of making patterns from a wax which can
be cast or injection-molded and can be expelled by being
heated as a pattern-making composition for use in a process
of making pieces of jewellery comprising one or more set
jewels, wherein a casting mold is made in that the pattern
is embedded in a refractory molding composition and the
pattern-making composition is subsequently expelled, metal

is poured into the casting mold and the piece of jewellery
is taken from the mold after the metal has solidified;
- a master pattern compor comprising empty settings for the
jewels is made;
- the master pattern which does not yet contain jewels is
used to make a master mold;
- a pattern is made from the pattern-making composition in
the master mold;
- the jewels are inserted into the pattern;
- the setting of the pattern is plastically deformed to fix
each jewel in its setting.
3. A process according to claim 1 or 2, characte-
rized in that the settings are thermally deformed.
4. A process according to claim 3, characterized in
that a tool which conforms to the top end of a given setting
is heated and engaged with the setting and the setting is
deformed in a single step in that pressure is applied to
the tool.
5. A process according to any of the preceding
claims, characterized in that the settings are only locally
deformed.
6. A process according to claim 6, characterized in
that in pin or tab settings only a part of the pins or tabs
is deformed.

Description

Note: Descriptions are shown in the official language in which they were submitted.


'` ' 212~
., ~: , .
Process of Making Set Cast Pieces of Jewellery
This invention relates to a process having the features ~
recited in the prior art part of claim 1. ~ ~ -
DE-38 24 574 Al describes a lost-wax melting process of
making pieces of jewellery. In the process a master pattern
of the piece of jewellery is made first and is used to make
a master mold. To make the mold, the master pattern may be
placed into a flask and a molding composition, e.g., a two- `
component silicone-rubber mixture, may be poured into the
flaks and cured therein. The resulting body may then be
dissected into two halves and the master pattern may
then be taken. Alternatively the master pattern may be
placed between two blocks of thermoplastic material,
which are then heated under pressure until they are ~ ~
15 plastically deformed and hug the master pattern so ~`
that a faithful impression of the master pattern is
formed in the two blocks (DE-35 46 188 Al). Because the
resulting bipartite master molds usually consist of ~ `
elastomeric material, they are sometimes called rubber
molds. A pattern-making composition, particularly a
wax, is then charged into such a master mold by casting
or injection molding. When the pattern-making composition
gas been cooled, the master mold is opened and the
pattern is taken. A plurality of patterns are usually ',
25 assembled to form a pattern tree, which is then embedded `~
into a refractory molding composition. The molding ~`
::.' ' -~'.'" ,
:' ' ::.'" ,'
, ~ ' "
. ~, ;.

2 1 2 ~ 1 ~ 2
- 2 -
composition will be regarded as "refractory" if it
withstands without deformation the action of a molten
metal from which the piece of jewellery is made. When the
pattern tree has been embedded in the refractory molding -~-~
S composition, the pattern-making composition of which the
pattern tree is made is expelled being heated. lf the
pattern-making composition is a wax or a low-melting
metal, it will be melted out (lost-wax casting processl.
If the pattern-making composition is a plastic, it will
be burnt out. The molten metal is then poured into the
casting mold thus made. To ensure that the metal from
which the pieces of jewellery are to be made will
penetrate into the last corners and branches of the
casting mold, the latter is rotated during the pouring
lS (centrifugal castingS or the pouring is assisted by the
~pplication of a vacuum (vacuum casting). When the tree
consisting of the pieces of jewellery has solidified and
cooled, it is removed and the pieces of jewellery are
separated from each other.
. ~ ~.'
~ ~
' .:; . ' `:
7 ''' '

f'` 212~1~2
-- 3 --
In the making of pieces of jewellery comprising
one or more set jewels it is also already known to embed
such jewels in the casting. For that purpose a master pattern
of the piece of jewellery in which the jewels are set is
made and that master pattern is used to make the master
mold, which is a negative replica of the piece of jewellery
and has openings for the jewels. The jewels for the piece
of jewellery are inserted into said openings of the master
mold, into which the pattern-making composition is then
poured or injected. The resulting pattern of the piece of
Jewellery is processed further as described hereinbefore.
But it is difficult to place the jewels into the master mold
in the correct positions and so to fix them that after the
pouring or injecting of the pattern-making composition the
~ewels will exactly have the positions which they are in-
tended to occupy in the subsequently made piece of jewellery.
The position of the jewels is often changed as they are em-
bedded in the poured or injected composition and the extent
to which the jewels are embedded in the injected composition
may vary from pattern to pattern. This may also be caused by -~
a variation of the Jewels from each other.
From French Patent Specification 1,599,866 it is
already known to embed jewels in a wax pattern, to assemble
such wax patterns in a wax pattern tree and to process them
further to make cast pieces of jewellery by a lost-wax
casting process. But in that case the pieces of jewellery
are not inserted on the wax pattern into a setting but are ~`
inserted into a wax pattern which has been made without a ~ -
setting. As a result, the cast piece of Jewellery also fails
to have a separate setting for the jewels.

r~ 2~2~1~2
4 :
.
From FR-A-2,366,812 it is known to make a master
pattern in which a jewel is set in a setting which has al-
ready its final shape, whereafter the jewel is carefully
taken out so that the setting is not changed, and the empty -
master pattern is ased to make a rubber mold, in which a
plastic pattern is then cast with a setting into which the
Jewel is inserted. Such patterns are then assembled to form
a pattern tree, which is embedded in gypsum, whereafter the
plastic is expelled and noble metal is cast into the re- -
sulting casting mold. That practice has the disadvantage
that the pattern must be made from a material which is so
elastic that jewels can be inserted into the finished set- ~
ting. Difficulties will arise with the usually employed P-
pattern waxes because they are lnelastic. For this reason
it is recommended in FR-A-2,366,812 to use a plastic, which
is expelled by a two-stage thermal process, namely, by melt-
ing followed by a shocklike heating to the temperature which
is required for the casting of the metal and at which the
plastic is decomposed. A further disadvantage resides in
that the jewel will not firmly be retained unless it has
exactly the same size and shape as the jewel that had been
inserted into the master pattern and this will not be the ~ `
case, as a rule, so that expensive subsequent work on the
cast piece of ~ewellery will be required.
It is an ob~ect of the invention so to improve
the process described first hereinbefore that exactly fit-
ting ~ewels in the piece of jewellery will be obtained in
the simplest possible manner without a need for subsequent
setting work on the piece of jewellery.
That object is accomplished by a process having
the features stated in claim 1 or 2. Desirable further fea-
tures of the invention are subject matters of the dependent
claims.

.~ :
r' 212~152
- 5
In the process in accordance with the invention,
just as in the known process, a master pattern of the piece
of jewellery to be made is malde first. That master pattern
has one or more settings in dependence on the number of
the intended jewels, but the jewels are not inserted into
the master pattern. For instance, in a pin setting the pins
intended to set the jewels are not bent inwardly but are
maintained in their original orientation. The master pattern,
into which a jewel has not yet been inserted, is then used
to make a negative mold as a master mold and a pattern of
the piece of jewellery is cast in that master mold. In that
case the pattern-making composition preferably consists of
a wax.
The pattern thus made is then provided with jewels
in that the ~atter are inserted into the settings provided
for that purpose. Because the pattern is 2 positive replica
of the piece of jewellery, the jewels can be inserted into '~
the settings from the entirely exposed top surface of the `~
piece of jewellery, as is the case with an original piece
of ~ewellery but it is not necessary to insert them into
difflcultly accessible openings of a negative mold (master
mold) in a difficult operation as in the lost-wax casting
process. The lnsertion of the jewels into the settings of
the pattern made of the pattern-making composition (parti-
cularly of a wax pattern) may be effected, e.g., by means of
a slender vacuum applicator, which is used to suck and hold
the ~ewel and to insert the jewel into the setting, the je-
wel is then left in the setting when the suction air has
been shut off. Thereafter the jewel needs only to be fixed
in the setting. The jewels are preferably fixed in their
settings in that the settings are softened by the action of
heat and are plastically deformed. This is preferably ac-
complished in that a tool which conforms to the top end of
the setting is heated and engaged with the setting and is

--`` 21251~2
- 6 -
forced against the jewel so that the setting is deformed
in a single step, This is possibIe not only wlth pln or
tab settings, which locally embrace the jewels as with fin-
~ers, but also with frame settings, which embrace the je~
wel throughout its periphery. In case of a frame setting
the tool for plastically deforming the setting will -~
suitably consist of a tool which has at its tip a frame-
like contact surface and that surface will be engaged with
the rim of the frame setting and forced against the peri-
pheral edge of the jewel.
In case of a pin setting or a tab setting, on the
other hand, it is desi~rable to employ a tool which has pro-
jections which correspond to the positions of the pins or
tabs and when the tool has been heated are placed on the
pins or tabs so that they are softened and flow and em~
brace the adjacent edges of the jewel; this can be accompli-
shed by a short contact with the tool. It has been found
that it is not necessary to deform all pins or tabs to fix
the jewels because a pin which has been deformed under the
action of heat will more closely contact the edge of the
Jewel than a metal pin which is forced against the edge of
the ~ewel in the conventional manner. For this reason only
part of the pins or tabs ~re preferably deformed în pin or
tab settings whereas the other pins or tabs are left unde-
formed. In that case the still undeformed pins will provide ~ -
the customary appearance of a conventional pin setting al-
though some pins have been deformed. In a pin setting com-
prising four pins per jewel, only two mutually opposite pins
will preferably be deformed in a setting that comprises six
pins.
The jewels can be so easily inserted into and
fixed in the model that said operation can perfectly be
performed even by unskilled labors after a brief instruction.

-' 212~1~2 - 7
For this reason the process in accordance with the inven-
tion can be adopted to special advantage for the industrial
mass production of pieces of jewellery. Even in the trial
phase of the process in accordance with the invention it
has been found that the costs of setting jewels can be
drastically reduced: In comparison with the conventional
technique, in which the jewels are inserted into the cast
ring rail, the setting costs can be decreased to 1/10 and
in comparison with the conventional lost-wax casting pro-
cess the costs can still be reduced to 1/4.
The further processing of the pattern made in
accordance with the invention is performed in the manner
which is known per se for the centrifugal casting or vacuum
casting of pieces of jewellery. This will be explained in
the example described hereinafter.
.: ~ .. .
A master pattern of metal is made in a manner
known per se for a piece of jewellery consisting, e.g., of
a ring, which is to be provided with a plurality of ~ewelsO
The master pattern has pin settings for the jewels but the
Jewels are not inserted. The master pattern is placed be-
tween two blocks of a thermoplastic silicone elastomer, which
are subsequently heated and forced against each other. As
a result, the silicone elastomer is plastically deformed to
hug the master pattern so that a faithful impression of the
master pattern i~s formed in the two blocks. The two blocks
which have thus been deformed constitute the two parts of a
master mold, into which a wax is subsequently injected.
When the wax has been cooled, the master mold is opened and
the wax pattern of the piece of jewellery is taken. There-
after a vacuum applicator is used to insert the intended
~ewels into and fix them in the settings which are formed ~ ;
in the wax pattern and consist each, e.g., of four pins.
This is accomplished in that a forklike tool having prongs

- 21251~2
-- 8 --
which are electrically heated and are spaced apart like
two mutually opposite pins is engaged with two mutually
opposite pins of a given setting and is slightly forced
against the latter so that the pins are softened and upset
and embrace the adjacent edge of the jewelO Thereafter, a
wax pattern :tree is made in a manner known per se from a
number of wax models thus made and is inserted into a flask,
into which a fine gypsum, such as alabaster, is poured.
When the gypsum has set, the flask is heated so that the
wax is molten out and the gypsum cast of the wax pattern
tree is left in the flask. The flask is heated to a tempe-
rature of about 750C and is inserted into a centrifugal ~
casting machine and a molten 14-carat gold alloy is poured ~ ;
into the flask and is permitted to solidify in the rotating
flask. When the flask has been cooled to about 40C the gyp-
sum is crushed to expose the cast tree. The pieces of je-
wellery are then severed from the tree and cleaned and optio-
nally polished.
The described process is particularly suitable
for pieces of ~ewellery comprising small jewels which can be
set with short pins having a length not in excess of 2.5
or 3 mm.

Representative Drawing

Sorry, the representative drawing for patent document number 2125152 was not found.

Administrative Status

2024-08-01:As part of the Next Generation Patents (NGP) transition, the Canadian Patents Database (CPD) now contains a more detailed Event History, which replicates the Event Log of our new back-office solution.

Please note that "Inactive:" events refers to events no longer in use in our new back-office solution.

For a clearer understanding of the status of the application/patent presented on this page, the site Disclaimer , as well as the definitions for Patent , Event History , Maintenance Fee  and Payment History  should be consulted.

Event History

Description Date
Time Limit for Reversal Expired 1997-12-03
Application Not Reinstated by Deadline 1997-12-03
Deemed Abandoned - Failure to Respond to Maintenance Fee Notice 1996-12-03
All Requirements for Examination Determined Compliant 1994-10-06
Request for Examination Requirements Determined Compliant 1994-10-06
Application Published (Open to Public Inspection) 1993-06-10

Abandonment History

Abandonment Date Reason Reinstatement Date
1996-12-03
Owners on Record

Note: Records showing the ownership history in alphabetical order.

Current Owners on Record
MANFRED MULLER
Past Owners on Record
None
Past Owners that do not appear in the "Owners on Record" listing will appear in other documentation within the application.
Documents

To view selected files, please enter reCAPTCHA code :



To view images, click a link in the Document Description column. To download the documents, select one or more checkboxes in the first column and then click the "Download Selected in PDF format (Zip Archive)" or the "Download Selected as Single PDF" button.

List of published and non-published patent-specific documents on the CPD .

If you have any difficulty accessing content, you can call the Client Service Centre at 1-866-997-1936 or send them an e-mail at CIPO Client Service Centre.


Document
Description 
Date
(yyyy-mm-dd) 
Number of pages   Size of Image (KB) 
Cover Page 1993-06-10 1 104
Abstract 1993-06-10 1 75
Claims 1993-06-10 2 132
Drawings 1993-06-10 1 13
Descriptions 1993-06-10 8 579
Fees 1995-11-08 1 57
Fees 1994-11-03 1 57
International preliminary examination report 1994-06-03 46 1,550