PRODUCTION METHOD OF PSEUDO-WOOD AND PSEUDO-STONE
FURNITURE OR ORNAMENT MATERIAL WITH NATURAL GRAINS
The present invention relates to a production method and, more
particularly, to a production method of pseudo-wood and pseudo-stone furniture
or ornament material with natural grains.
A conventional method for making furniture or wooden ornament
material comprises using a machine to work the wood material into many parts.
Then, the parts are bonded by glue. Then, the parts are secured by screws and
bolts. Finally, paint is sprayed on the parts to produce the furniture or
ornament
material. However, such a method for making furniture or wooden ornament
material has complicated working procedures, needs a large amount of wood
material, and has a high cost of fabrication. In addition, a large amount of
waste
material is produced during the manufacturing process, thereby causing
consumption of the forest source, and polluting the ecology and the
environment.
The primary objective of the present invention is to provide a
production method of pseudo-wood and pseudo-stone furniture or ornament
material with natural grains.
In accordance with the present invention, there is provided a production
method of pseudo-wood and pseudo-stone furniture or ornament material with
natural grains, comprising:
CA 02948558 2016-11-16
(1) providing wood and stone with natural grains, or furniture or
ornament material made of designed wood and stone with natural grains, to
function as a model of production;
(2) mixing and evenly stirring silica gel and a hardener to form a
mixture, then brushing the mixture on the model evenly, then spreading a
gauze,
then brushing the mixture again, and repeating three times during 4-10 hours
until
the silica gel has a thickness reaching 5-10mm, to cure and form an interior
mold
of production;
(3) using resin to make an exterior mold on the interior mold which is
cured, with the exterior mold having a shaping function;
(4) adding a modifier with a mass proportion of 1-8% into a magnesium
chloride solution with 15-35 Baume degrees, and mixing and stirring evenly to
form a magnesium chloride mixture solution;
(5) mixing magnesia with the magnesium chloride mixture solution
according to a mass proportion of 1-2:1, then adding sawdust powder, glass
fiber
and talcum powder, with a mass proportion of 10-20%, and placing the above
substances into a blender and blending to form a paste mixture;
(6) removing the model, then wiping a layer of release agent on the
interior mold and the exterior mold, then adding the paste mixture in the
interior
mold, then spreading one layer or two layers of fiber felt, then trimming
flat, then
2
CA 02948558 2016-11-16
brushing the paste mixture, then trimming flat again, and placing a framework
and
shaping, to make magnesia furniture or ornament material with a thickness of
5-10mm;
(7) drying the magnesia furniture or ornament material during 2-8 hours,
then stripping, then placing the magnesia furniture or ornament material on a
platform or in a drying space to perform an oxidation process during 7-30
days,
and trimming the magnesia furniture or ornament material to a determined
extent;
(8) using a water-based paint to prepare proper colors according to the
natural grains of the magnesia furniture or ornament material, and manually
coloring the magnesia furniture or ornament material to make required colors;
and
(9) providing legs and bases under the magnesia furniture or ornament
material, to assemble and produce furniture or ornament material with natural
grains.
Preferably, in the step (2), the silica gel has a mass proportion of 3-5% in
the mixture, and the hardener has a mass proportion 0f95-97% in the mixture.
Preferably, in the step (4), the modifier is prepared by a group of
substances including: potassium carbonate with a mass proportion of 10-20%,
aluminum sulfate with a mass proportion of 10-20%, silicon dioxide with a mass
proportion of 30-50%, ferrous sulfate with a mass proportion of 10-20%,
phosphoric acid with a mass proportion of 5-10%, oxalic acid with a mass
3
CA 02948558 2016-11-16
proportion of 5-10%, ferric oxide with a mass proportion of 5-10% and aluminum
oxide with a mass proportion of 5-10%; and the step (4) further includes using
water to dilute the prepared modifier to have 15-35 Baume degrees.
Preferably, in the step (5), the mass proportion of the sawdust powder,
the glass fiber and the talcum powder is 1:1:1.
Preferably, in the step (6), the release agent is floor wax or detergent.
Preferably, in the step (6), the framework is made of iron or wood.
A production method of pseudo-wood and pseudo-stone furniture or
ornament material with natural grains in accordance with the present invention
comprises:
(1) providing wood and stone with natural grains, or furniture or
ornament material made of designed wood and stone with natural grains, to
function as a model of production;
(2) mixing and evenly stirring silica gel and a hardener to form a
mixture, then brushing the mixture on the model evenly, then spreading a
gauze,
then brushing the mixture again, and repeating three times during 4-10 hours
until
the silica gel has a thickness reaching 5-10mm, to cure and form an interior
mold
of production;
(3) using resin to make an exterior mold on the interior mold which is
cured, with the exterior mold having a shaping function;
4
CA 02948558 2016-11-16
(4) adding a modifier with a mass proportion of 1-8% into a magnesium
chloride solution with 15-35 Baume degrees, and mixing and stirring evenly to
form a magnesium chloride mixture solution;
(5) mixing magnesia with the magnesium chloride mixture solution
according to a mass proportion of 1-2:1, then adding sawdust powder, glass
fiber
and talcum powder, with a mass proportion of 10-20%, and placing the above
substances into a blender and blending to form a paste mixture;
(6) removing the model, then wiping a layer of release agent on the
interior mold and the exterior mold, then adding the paste mixture in the
interior
mold, then spreading one layer or two layers of fiber felt, then trimming
flat, then
brushing the paste mixture, then trimming flat again, and placing a framework
and
shaping, to make magnesia furniture or ornament material with a thickness of
5-10mm;
(7) drying the magnesia furniture or ornament material during 2-8 hours,
then stripping, then placing the magnesia furniture or ornament material on a
platform or in a drying space to perform an oxidation process during 7-30
days,
and trimming the magnesia furniture or ornament material to a determined
extent;
(8) using a water-based paint to prepare proper colors according to the
natural grains of the magnesia furniture or ornament material, and manually
coloring the magnesia furniture or ornament material to make required colors;
and
5
CA 02948558 2016-11-16
(9) providing legs and bases under the magnesia furniture or ornament
material, to assemble and produce furniture or ornament material with natural
grains.
In the step (2), the silica gel and the hardener are mixed according to a
determined proportion. Preferably, the silica gel has a mass proportion of 3-
5% in
the mixture, and the hardener has a mass proportion of 95-97% in the mixture.
In
addition, the mixture is applied on the model by a brush.
In the step (4), the modifier is prepared by a group of substances
including: potassium carbonate with a mass proportion of 10-20%, aluminum
sulfate with a mass proportion of 10-20%, silicon dioxide with a mass
proportion
of 30-50%, ferrous sulfate with a mass proportion of 10-20%, phosphoric acid
with a mass proportion of 5-10%, oxalic acid with a mass proportion of 5-10%,
ferric oxide with a mass proportion of 5-10% and aluminum oxide with a mass
proportion of 5-10%. In addition, the step (4) further includes using water to
dilute the modifier that has been prepared to have 15-35 Baume degrees.
In the step (5), the mass proportion of the sawdust powder, the glass
fiber and the talcum powder is 1:1:1. In addition, the glass fiber provides a
reinforcing function.
6
CA 02948558 2016-11-16
In the step (6), the framework is made of iron or wood. In addition, a
simple ornament does not need the framework. In addition, the release agent is
floor wax or detergent.
In the step (9), the legs and bases are made of iron or wood and are
designed professionally.
In the preferred embodiment of the present invention, the production
method of pseudo-wood and pseudo-stone furniture or ornament material with
natural grains in accordance with the preferred embodiment of the present
invention comprises:
(I) providing wood and stone with natural grains, or furniture or
ornament material made of designed wood and stone with natural grains, to
function as the model of production;
(2) mixing and evenly stirring the silica gel and the hardener according
to a determined proportion to form the mixture (the silica gel has a mass
proportion of 3-5% in the mixture, and the hardener has a mass proportion of
95-97% in the mixture), then using the brush to brush the mixture on the model
evenly, then spreading the gauze, then brushing the mixture again, and
repeating
three times during 4-10 hours until the silica gel has a thickness reaching 9-
10mm,
to cure and form the interior mold of production;
7
CA 02948558 2016-11-16
(3) using the resin to make the exterior mold on the interior mold which
is cured, with the exterior mold having a shaping function;
(4) adding water into the magnesium chloride at the normal temperature
to prepare the magnesium chloride solution of 20 Baume degrees, with the
magnesium chloride solution being prepared one day before production;
adding the modifier with a mass proportion of 5% into the magnesium
chloride solution, using water to dilute the modifier to have 20 Baume
degrees,
and mixing and stirring evenly to form the magnesium chloride mixture
solution;
the modifier being prepared by the group of substances including:
potassium carbonate with a mass proportion of 10%, aluminum sulfate with a
mass proportion of 10%, silicon dioxide with a mass proportion of 40%, ferrous
sulfate with a mass proportion of 10%, phosphoric acid with a mass proportion
of
8%, oxalic acid with a mass proportion of 8%, ferric oxide with a mass
proportion
of 7% and aluminum oxide with a mass proportion of 7%;
(5) mixing the magnesia with the magnesium chloride mixture solution
according to a mass proportion of 1 .8:1, then adding the sawdust powder, the
glass fiber and the talcum powder, with a mass proportion of 15%, and placing
the
above substances into the blender and blending to form the paste mixture;
the mass proportion of the sawdust powder, the glass fiber and the
talcum powder being 1:1:1;
8
CA 02948558 2016-11-16
(6) removing the model, then wiping a layer of release agent on the
interior mold and the exterior mold, then adding the paste mixture in the
interior
mold, then spreading one layer or two layers of fiber felt, then trimming
flat, then
brushing the paste mixture, then trimming flat again, and placing the iron
framework (a simple ornament does not need the framework) and shaping, to
make magnesia furniture or ornament material with a thickness of 8-9mm;
(7) drying the magnesia furniture or ornament material during 8 hours,
then stripping, then placing the magnesia furniture or ornament material on
the
platform or in the drying space to perform an oxidation process during about
10
days (the magnesia furniture or ornament material is placed on the platform
during about 30 days if the temperature is too low), and trimming the magnesia
furniture or ornament material to the determined extent;
(8) using the water-based paint to prepare proper colors according to the
natural grains of the magnesia furniture or ornament material, and manually
coloring the magnesia furniture or ornament material to make required colors;
and
(9) providing legs and bases, made of iron or wood and designed
professionally, under the panel of the magnesia furniture or ornament material
that is colored, to assemble and produce the product of the furniture or
ornament
material with natural grains.
9
CA 02948558 2016-11-16
In conclusion, the characteristic of the present invention is in that, the
magnesia, the magnesium chloride, the water and the glass fiber are the
primary
staple. Then, a determined amount of modifier, sawdust powder and talcum
powder is added into the primary staple. Then, the mold and the framework are
operated according to the determined steps. Then, the primary staple is
shaped.
Then, the primary staple performs an oxidation process to form the product.
Accordingly, the product is directly manufactured by the mold, without
needing multiple and complicated working steps, thereby simplifying the making
procedures, reducing the working time, and decreasing the cost of fabrication.
In
addition, the product contains the natural grains of wood or stone without
needing
special sculpture, thereby saving the manual labor, and enhancing the
aesthetic
quality of the product. Further, the product only uses little wood material,
thereby
largely reducing consumption of the forest source, and protecting the
ecological
environment. Further, the product does not contain any harmful substance, such
as
benzene, formaldehyde or the like so that it will not do harm to the user.
Further,
the product is waterproof, dampproof, mothproof and mildewproof, and is not
distorted or deformed. Further, the product has heat isolating, soundproof and
electricity insulating functions.
Although the invention has been explained in relation to its preferred
embodiment(s) as mentioned above, it is to be understood that many other
CA 02948558 2016-11-16
possible modifications and variations can be made without departing from the
scope of the present invention. It is, therefore, contemplated that the
appended
claim or claims will cover such modifications and variations that fall within
the
true scope of the invention.