STRATIFIE THERMOFORMABLE IMPRIME A PROTECTION ACCRUE CONTRE LA FALSIFICATION

PRINTED THERMOFORMABLE LAMINATE WITH INCREASED SECURITY AGAINST FORGERY

Abrégé français

L'invention concerne un stratifié thermoformable imprimé, constitué d'au moins deux feuilles de plastique et dans lequel l'élément imprimé est placé entre des feuilles de plastique à l'intérieur dudit stratifié de manière à augmenter la protection contre la falsification. Des stratifiés préférés présentent la structure suivante : feuille A / impression / produit de contrecollage / feuille C feuille A / impression / produit de contrecollage / feuille B / produit de contrecollage / feuille C feuille A / impression / produit de contrecollage / feuille B / produit de contrecollage / impression / feuille C.

Abrégé anglais

The invention relates to a printed thermoformable laminate comprised of at
least two plastic films. The printing is placed between plastic films inside
the laminate in order to increase protection against forgery. Preferred
laminates have the following structure: film A / print / laminating agent /
film C; film A / print / laminating agent / film B / laminating agent / film
C, and; film A / print / laminating agent / film B / laminating agent / print
/ film C.

Revendications

Claims
1. Thermoformable laminate made of at least two plastics material films with
printing, characterised in that the printing is arranged inside the laminate
between the plastics material films to increase the security against forgery.
2. Thermoformable laminate according to claim 1, characterised in that the
laminate is constructed as follows:
film A / print / laminating means / film C
film A/ print / laminating means / film B/ laminating means / film C
film A/ print / laminating means / film B/ laminating means / print /
film C.
3. Thermoformable laminate according to claim 2, characterised in that the
films A, B and/or C are thermoformable plastics material films or
combinations of these plastics material films based on chlorinated
hydrocarbons, chlorofluorocarbons, polyolefins,
polyethyleneterephthalates, polyacrylonitriles, cycloolefin copolymers,
cycloolefin polymers, polysulphones or biologically degradable plastics
materials.
4. Thermoformed container, in particular blister base part, or beaker made of
a thermoformable laminate according to any one of the preceding claims.
5. Use of thermoformed containers and beakers according to claim 4 for the
packaging of pharmaceutical and medical products.

Description

CA 02620504 2008-02-27
Printed thermoformabMe laminate with increased security against forgery
The invention relates to a printed thermoformable laminate made of at least
two
plastics material films.
Thermoformable plastics material laminates may be printed for customer
information before or after forming. The printing of the laminates before the
thermoforming into containers or beakers takes place prirriarily on the
container
wall with current printirig methods. If the plastics material laminate is
printed
before the thermoforming the printing may detach to a greater or lesser extent
from the laminate surface during forming or during the logistics because of
the
reduced adhesion of the printing dyes to the background, as a function of the
degree of forming.
In the two cases of conventional printing, the print is located on the outside
of the
laminate surface formirig the packaging and is therefore easily accessible for
forgeries, in that the print can be removed from the packaging and can easily
be
replaced by printing on new information.
When using pre-printed laminates, there is also the possibility that these may
be
produced by forgers, as plastics material films and laminates made of plastics
materials are available to an almost unlimited extent commercially.
The invention is based on the object of providing a thermoformable laminate of
the type mentioned at the outset with a printing such that, in comparison to
the
printed thermoformable laminates according to the prior art, a substantially
higher
degree of security against forgery is produced.
The fact that the printing is arranged between adjacent plastics material
films to
increase the security against forgery leads to the achievement of the object
according to the invention.
The followirig structures are preferred for the laminates according to the
invention:

CA 02620504 2008-02-27
film A/ print / laminating means / film C
film A/ print i laminating means / film B/ laminating means / film C
film A/ print / laminating means / film B/ laminating rrieans / print / film
C.
The films A, B and C; are thermoformable plastics material films based on
chlorinated hydrocarboris, such as polyvinyl chloride and polyvinylidene
chloride,
chlorofluorocarbons, for example ACLARO, polyolefins,
polyethyleneterephthalates, polyacrylonitriles, for example BAREX ,
cycloolefin
copolymers, cycloolefiri polymers, polysulphones or biologically degradable
plastics materials, or combinations of these plastics materials in the
laminate.
PVDC may be a film or a coating.
The total thickness of the laminates is 150 to 500 pm and also 90 to 150 pm in
PVC/PE laminates.
The lamination takes place with laminatirig adhesives based on water, with
solvent-based or solvent-free laminating adhesives and/or by extrusion
lamination
as monoextrusion or coextrusion. In the case of COC or COP laminates with PE
or PP, a lacquer lamination or else the production of a partial laminate by
coextrusion is recommended.
The interlaminar bond of the individual layers should be at least 2 N/15 mm.
When using dyed films for the printing, the colour of the printed image may be
changed by a corresponding choice of colour. For example, blue printing of a
film
which is dyed yellow leads to a printed image which appears green. The
security
against forgery of printed laminates cari be further iricreased with colour
combinations of this type.
The preferred film combinations for the laminates according to the invention
are
compiled in Table 1. The abbreviations of the plastics materials on which the
films are based mean~
2

CA 02620504 2008-02-27
PVC polyvinyl chloride
PVDC polyvinylidene chloride
PAN polyacrylonitrile
PE polyethylene of various densities, including the metallocenes
PP polypropylenes, including the rnetallocenes
COC cycloolefir copolymer
COP cycloolefir polymer
PSU polysulphone
PCTFE polychlorotrifluoroethylene
EVOH ethylene vinyl alcohol
PGA polyglycolic acid
Containers thermoformed from the laminate, in particular blister base parts,
or
beakers, preferably for packaging pharmaceutical and medical products are a
preferred application area of the thermoformable laminate according to the
invention.
3

CA 02620504 2008-02-27
Table 1: Preferred laminate structures
Film A Film B Film C
Laminate number
1 _ PVC PVC
- - - ~ ~
2 PVC PCTFE
3 PVC PAN
- -~ PE - {
PVC PVDC
COC or COP
k6 7 } PVC PVC PVC PVC
PVC PCTFE PVC
- -- - --- - -- - - ---~- -- - ----- -_ _ _
PVC PAN PVC
-- ~--- -- -- -
PVC EVOH or PGA PVC
11 PVC PE PVC ~
- - - - -
12 PVC PE PVDC - ------
13 PVC COC or COP PVC
14 PVC COC or COP pp
---_ _ - - _ I ----
-
PVC COC or COP PVDC
- , . . - - - 16 PVC COC or COP PCTFE
17 PVC COC or COP PAN
18 PVC PVC- PE
-- - -- -
19 P PP
P _ - f PCTFE
21 pP { PVDC
22 PP COC or COP
~
23 pp PCTFE
PP
24 PP 1 EVOH or PGA i, PP
PP COC or COP PP
-
- - --- ---
PAN PP
! 26 PP
.27 r pp COC or COP PVDC
-----
28 --PP COC or COP - -
PCTFE
-
-
29 PET !PET
-----
I'ET PCTFE ,
31 -PET PVDC
- -- -- ------ --
32 T
IDSU PVC
--- - - _ ~_ - --- -~ - - -
33 I SU PET
- - - -
34 I'SU pp 35 PSU COC or COP PP
- _ ---- ----- -- - J
36 I'SU PVC PCTFE
37 PSU PVC PVDC
38. PSU ! PET PCTFE
4