I. BACKGROUND 0~ ~HE INVENTI~N
1. Field of the Invention
This invention relates to an improved process for
the polymerization of olefins to provide linear polymers
and copolymers, said process employing an improved catalyst
comprising tetra(neophyl) zirconium, or its reaction pro-
ducts with metal oxides, for use therein. More specifically,
the metal oxide can be an oxide selected from a metal o~
Groups II(a), III(a), IV(a), or IV(b) of the Bohr Periodic
Table of the Elements. -~
2. Prior Art
In 1954 and 19~5 pioneering advances in olefin
polymerization catalysts were disclosed by Karl Ziegler and
associates at the r~ax-Planck Institute for Coal Research
in MUlheim, Germany, and by Arthur Anderson and associates
in the laboratories of E. I. du Pont de Nemours and
Company in Wilmington, Delaware. These new catalyst
systems, now frequently termed coordirlation catalysts,
were based on transition metal salts (e.g. titanium,
zirconium or vanadium halides) which had been converted
into reduced valence states by reaction with a variety of
alkylating or arylating substances, usually simple organo-
metallic compounds of a metal of Groups I, II or III of
the Periodic Table of Elements (the Bohr long form).
More recently some more stable organometallic
transition metal complexes, usually including a halide ~ -
anionic ligand or a neutral Lewis Base ligand, have been
disclosed in a number of patents. Illustrative are U.S. -
Patents 3,681,317, 3,740,384, 3,738,944 and British Patent
1,314,828 which involve tetra(benzyl)-transition metal
- 2 -
lOS~lS4
':
compounds (e.g. tetra(benzyl) zirconium) complexed with
anionic ligands (e.g. halide) and/or neutral ligands (e.g.
pyridine) as ethylene polymerization catalysts. In certain
cases the reaction products of tetra(benzyl)-zirconium
compounds with inorganic oxides free of absorbed water but
containing surface HO- groups are disclosed as catalysts
for the polymerization of olefinic hydrocarbons. Reason-
able thermal stability is achieved with these substances.
They apparently yield high molecular weight polyethylene
but the polymerization rate and efficiency and polymer
yield obtained with those catalysts in processes for the
polymerization of ethylene are generally not as good as
with classical coordination catalysts.
II. SUM~ARY OF THE INVENTION
There has been discovered a catalyst system for
the polymerization of olefins in hyd~ocarbon medium which
comprises a solution in inert hydrocarbon solvent of
tetra(neophyl) zirconium or, preferably, a suspension of
a metal oxide of a metal of Groups II(a), III(a), IV(a) or
IV(b), preferably alumina, having chemically bonded onto
its surfaces neophyl zirconium metallate prepared, prior
to contacting with an olefin monomer, by reacting a hydro-
carbon solution of a tetra(neophyl) zirconium with a sus-
pension in hydrocarbon medium of a surface hydrated metal ~-
oxide free from any merely absorbed H2O. Representative
examples of suitable oxides are A12O3, ~iO2, SiO2, MgO,
coprecipitated A12O3.ZrO2 and coprecipitated SiO2.A12O3,
in each case having a surface area in the range of 10-500
m2/g, as measured by N2 adsorption. Preferred and
especially active metal oxide supports have been prepared
3 --
t
lOS4154
from fumed aluminas, such as those sold by ~egussa ("Alumina
C") and Cabot Corporation ("Alon~ G").
III. DESCRIPTION OF THE DRAWINGS
Figure I is a schematic drawing of the continuous
i olefin polymerization process of this invention which ln- -
: cludes the preparation of the catalyst, injection of the
.. catalyst into the polymerizer and continuous recovery of
polyolefin therefrom.
Figure II-A shows the nuclear magnetic resonance
spectrum (60MC) of tetra(neophyl) zirconium. On Figure
II-A, the absorption peak due to the methylene protons is
indicated at (1), that due to the methyl protons at (2)~
and that due to protons on the aromatic ring at (3); these
protons can be identified by reference to the chemical
formula:
2) (3) (3)
-Zr ~ Cl
3 H H
(3) (3) ~~ 4
(2) -
In Figure II-B there is shown for comparison
the NMR spectrum obtained in the same manner, of tetra. ~-
(benzyl) zirconium.
(2) (3) ~:
Zr ~ C112~ H (3)
(1)'
H H
- (2) (3) - 4
.
` lOS~154
On Figure II-B the absorPtion due to the methylene protons
is again shown at (l); there are, of course, no methyl pro- -
tons, but two bands for the protons on the aromatic ring
are seen at (2) and (3) corresponding to protons at posi-
tions indicated by (2) and (3) on the above formula.
IV. DESCRIPTION OF PREFERRE~ EMBODIMENTS
It has been discovered that in order to obtain
the most active catalyst of this invention, it is preferred
to modify the crystalline form of the alumina and control
the extent of hydration on its surfaces prior to reaction
with tetra(neophyl) zirconium by activating the alumina by
heat treatment under a flow of an inert anhydrous gas (e.g.
N2) at a temperature in the range of 900 to 1100C. for 1
to 10 hours followed by hydration to the extent of 3% to
5% by contact with an atmosphere containing water vapor
followed by dehydration by heating at 300 to 500C. for 1
to 10 hours to provide an alumina containing 0.5% to 1.5%
water as HO- groups on the surfaces of the alumina. The
preferred catalyst, neophyl zirconium aluminate, bonded
onto the surfaces of the alumina, is then prepared
by contacting a suspension of the hydrated alumina in
anhydrous inert hydrocarbon medium with from 0.05 to 0.6,
preferably 0.15 to 0.35, millimoles of tetra(neophyl)
zirconium, dissolved in any anhydrous inert hydrocarbon
solvent, per gram of suspended A12O3 at 0 to 100C. until
the reaction is complete~ ` '
It has been found that the reaction product of
; tetra(neophyl) zirconium with a hydrated metal oxide tends
to undergo spontaneous transformation, particularly at
temperatures of 50 to 100C. and above, to thermally
~O5~lS~
` stable, lower valence states in which the zirconium is
present at least in part at a valence of three. However,
such prior transformation is not necessRry if the catalyst is
to be employed in polymerization processes conducted at
temperatures above 100C.
The polymerization of olefins with the catalysts
of this invention can be conducted at temperatures in the
range of 10 to 300C. at pressures varying, with tempera-
ture, from atmospheric to 1000 atmospheres or above, the
pressure being selected high enough to keep the monomers in
solution. For ethylene polymerization of a slurry type,
temperatures in the range of 10 to 110C. are suitable.
For the solution polymerization of ethyleneJ which is pre-
ferred, temperatures can range from 125C to 300C, but pre-
ferred temperatures are in the range of 130 to 270C. Any
inert hydrocarbon can be employed as a polymerization medium. -
Suitable classes include n-alkanes, cycloalkanes and
aromatic hydrocarbons, representative example being propane,
n-hexane, cyclohexane, n~heptane, and toluene. Hydrogen
can be added to the polymerization zone to control and
limit the molecular weight of the polyolefin produced.
Tetra(neophyl) zirconium, otherwise identified as
tetra kis(2-methyl, 2-phenylpropyl) zirconium, can be pre-
pared by the reaction of a zirconium tetrahalide, preferably
ZrC14, with an organometallic compound of a metal ~f Groups
I, II or III of the Periodic Table of the Elements accord- -
ing to Bohr (see T. Moeller, "Inorganic Chemistry", p. 122)
in which the organic radicals attached to the metal are
neophyl radicals. A convenient method of preparation is
the reaction of an ethereal solution of the neophyl
-- 6 --
. .
lOS4154
Grignard reagent ~ith ZrC14 according to the following
reaction:
CH3 r CH3
4 ~C-C~MoCl + ZrCl~ C-c~12--~r + ~ Cl
CII3 ~_ C~13 _
The reaction of the Grignard reagent with the
ZrC14 is most conveniently carried out in an anhydrous
liquid medium by adding powdered ZrC14 as a solid or slurry
- in an inert anhydrous liquid to a solution of the neophyl
Grignard reagent. The temperature in the reaction vessel
should be maintained in the range of 0 to 70C. Mainte- -
nance of dry, oxygen-free conditions during the addition
and reaction is essential. An ethyl ether-toluene mixed
solvent is suitable as the medium. The resultant tetra-
(neophyl) zirconium is soluble in hydrocarbon solvents or
ether-hydrocarbon mixed solvents, and the solution is
readily separated from the precipitated MgC12 by decanta-
tion or f'iltration. Pure crystalline tetra(neophyl)
zirconium can be recovered by evaporation of the solvent
followed by recrystallization from a hydrocarbon solvent
such as toluene by warming, cooling and filtration. The
resultant purified crystals are cream to light tan in
color and melt at 67-68C. (hot stage) or 69C. (DSC
method). The crystalline tetra(neophyl) zirconium is
thermally stable and can be stored without decomposition
at 25C. for many hours or at -35C. ~or many weeks.
Thermolysis studies showed that very little decomposition,
as measured by weight loss, occurred when tetra(neophyl)
zirconium was heated at 10C./min. until a~ter temperatures
above 100C. were reached. This thermal stability was
.
1054154
unexpected in view of the known instability of many other
tetrathydrocarbyl) zirconium compounds such as tetra(alkyl)
zirconiums. Thermal decomposition of tetra(neophyl)
; zirconium at temperatures above 100C. yields primarily t-
butyl benzene and a dark residue readily oxidized to a
white zirconium oxide by air.
The unique structure of tetra(neophyl) zirconium
is also revealed by its nuclear magnetic resonance spectrum
(NMR) Figure II-A, which shows methylene protons at 8.93~ ,
methyl protons at 8.76 ~ and phenyl protons at 2.7r
Since the NMR spectrum of tetra(neophyl) zirconium shows
no broadening of the peak due to the phenyl protons, it
appears that no interaction between the -electrons of the
benzene ring and the d-orbitals of zirconium occurs in this
compound distinguishing it from the -allyl and benzyl
zirconium compounds of the prior art which show such inter-
action (see Figure II-B). The absence of such interaction
changes the chemical reactivity of the zirconium-hydrocarbon
bond. Also, the greater stability of tetra(neophyl) zir-
conium, compared to many other tetra(hydrocarbyl) zirconiumcompounds (e.g. tetra(alkyl) zirconium) must be associated
with the absence of a hydrogen atom on the carbon beta to
the metal; this reduces the tendency for decomposition via
~-hydride transfer and olefin elimination.
Rather surprisingly, tetra(neophyl) zirconium
alone has been found to be an effective~-catalyst for the
polymerization of ethylene and other a-olefins to yield
high molecular weight, solid, linear polyolefins. While
not wishing to be bound by any particular theory of the
mechanism, it is believed probable that, upon contact of
-- 8 --
.
:
~054154
the tetra(neophyl) zirconium with a polymerizable olefin
under polymerization conditions, a metathesis occurs where-
by one or more neophyl radicals are replaced by the alipha-
tic radicals corresponding to the olefin to be polymerized,
and, thereupon~ there occurs a partial decomposition due to
the known instability of Zr-aliphatic bonds so that the
zirconium is then reduced in valence to the lower-valence
forms (ZrII and ZrIII) known to be active as coordination
catalysts in the polymerization of olefins.
Even more active catalysts for the polymerization
of olefins are obtained by reacting tetra(neophyl) zircon-
ium with a hydrated metal oxide of the classes previously
defined. In the course of this reaction, particularly as
- the temperature of the reactants is raised, the zirconium-
metal oxide reaction product undergoes partial decomposi-
tion to provide neophyl zirconium in the active, lower~
valence states, chemically bonded to the surfaces of the
~ metal oxide which can then be dispersed in an inert hydro-
; carbon and passed to a polymerization zone where the
catalyst contacts the olefin monomer and converts it to
a high molecular weight, solid, linear polyolefin. If
desired, these supported zirconium neophyl metal oxide
catalysts can also be used as fluldized beds to polymerize
gaseous olefins to high molecular weight polyolefins.
The preferred catalyst, because of its stability
and the high rates of olefin polymerization obtained with
this catalyst, in a process for the polymerization of
ethylene and/or other l-olefins~ is neophyl zirconium
aluminate supported on and bonded to fumed alumina having
a surface area in the range of 10 to 500 m2/g, as measured
_ g _
"
1054154
by N2 adsorption. Prior to injection of the catalyst sus-
pended in an inert hydrocarbon solvent, into the polymeri-
zation zone, the zirconium may,due to spontaneous rearrange-
ments, have a reduced valency and be at least in part in
the Zr(III) valence state although some Zr(II) and Zr(IV)
may also be present.
The polymerization process is carried out in an -
inert, substantially anhydrous hydrocarbon medium. The
temperature employed may range from about 20C. to 300C.,
depending on the monomer or monomers to be polymerized and
upon whether a slurry or a solution polymerization process
is to be used. In the case of the polymerization of ethyl-
ene, either homopolymerization or copolymerization with
other olefins, the preferred temperature is in the range of
130-270C. where a single phase, solution polymerization
process occurs at maximum rates and high efficiency (yield
of polymer per unit of zirconium catalyst). Propylene is
preferably polymerized at lower temperatures in the range
of 50 to 150C.when cr~stalline polypropylene is ~he d~ed
product, although higher temperatures can be employed.
The pressure employed is not critical so long as
it is sufficient, at the temperature chosen, to prevent --
boiling of the hydrocarbon solvent and maintain the MOnO-
mers employed in solution in the solvent. Thus the pres-
sure may range from atmospheric to 1,000 atm. and above at
the highest temperatures of operation of the process.
In order to achieve optimum catalytic activity
it is preferred that there be employed an alumina ha~ing
a surface area of 10 to 500 m2/g, free from absorbed water
but containing hydroxyl groups generally randomly
-- 10 --
~, . , -
~054154
distributed on its surfaces. Preferably this alumina sup-
port is most readily produced by activation of fwned
alumina (a product obtained by burning aluminum chloride in
the presence of water vapor) by heating in a stream of dry
N2 at temperatures in the range of 900-1100C. for a
period in the range of 1 to 10 h~urs. This treatment not
only removes water and residual chloridc from the fumed
alumina but alters the morphology of the crystalline alumina
from predominantly gamma-alumina to a particular mixture
of the gamma-, delta-, theta-, and alpha-forms. The re-
sultant mixture of crystalline forms is essential for ob-
taining, in the subsequent reactions with tetra(neophyl)
zirconium, the unique chemical composition of the zirconium
neophyl aluminate necessary to produce the optimum catalyst
which exhibits the unexpected and surprising activity and
efficiency characteristic of the preferred polymerization
process of this invention.
The fumed alumina, activated as described above,
is then subjected to partial hydration by contact with an
atmosphere comprising some water vapor until a minor pro-
portion of water has reacted with the alumina surface,
conveniently about 3% to 5% by weight water of hydration.
This rehydrated alumina may then be partially dehydrated
by heating at a temperature in the range of 300 to 500C.
for from 1 to 10 hours, the time required being in the
lower portion of the range at the higher; temperatures in
the range of temperatures. The final product contains from
0.5% to 1.5% by weight water as H0-groups distributed on
the surfaces of the alumina. This second heat treatment
not only assures that no merely absorbed molecular H20
-- 11 --
1054154
remains on the surraces Or the alumina but also elîminates
any large clusters of H0-groups on the surfaces lea~ing
randomly distributed on the A12O3 surfaces pairs and rela-
tively isolated H0-groups as reaction sites.
The high temperature activation removes essen-
tially all H20 and HO-groups from the alumina, decreases
the amount of residual chloride from an initial 0.7% to
0.2% by weight and, very importantly, converts a portion
of the original crystalline ~amm~,A1203 to the more active
delta-and theta-forms. Partial rehydration with water
vapor in a moist atmosphere replaces hydroxyl groups on the
A1203 surfaces.
The final drying at about 400C. reduces the con- -~
; centration of H0-groups on the surfaces of the A1203 to an
optimum value in the range of 0.5 to 1.5% by weight water,
thus providing isolated single and pairs of HO-groups on
the alumina surfaces, making these surfaces most suitable
for reaction with tetra(neophyl) zirconium in solution.
The preferred catalyst is next prepared by mixing
together a suspension of the activated, hydroxylated alumina
; in anhydrous mineral oil with a solution in hydrocarbon
solvent of tetra(neophyl) zirconium. In general, the pro- ~ -
portion of tetra(neophyl) zirconium employed is at least
0.05 millimoles per gram of A1203, preferably 0.15 to 0.35 ~ -
millimoles per gram A1203, or other metal oxide. Larger
proportions are operable but provide no advantage since
they provide no enhancement of catalyst activity.
The reaction between tetra(neophyl) zirconium and
hydroxylated alumina can be conducted at temperatures in
the range of 0 to lOO~C., depending on the time allowed.
- 12 -
~ ~ (
~054154
Upon mixing the suspension of alumina with the solution of
tetra(neophyl) zirconium, a reaction occurs between the HO-
groups on the surfaces whereby Zr-O-Al chemical bonds are
formed with the elimination of approximately 2.5 of the 4
hydrocarbyl radicals originally bonded to the zirconium.
The reaction may be approximately described by the equations
, ~
__.. .- - - . .. _ _ . :
___
'
.
.
,
. _ ... _ .__
- 13 _
, .
~054~5~
(A) and (B):
0/
A l-OH CH3
(A) (~ + <~ C--CH2- -Zr- >
Al-OH CH3 4
-. O\ '
zr~CH2-C ~> + 2 CH3-C ~3
~1-0 3 2
(B) + 2[~>C-CH2~Zr~
Al-OH CH
~.......... \ : .
Al-O-Zr~cH2-c ~3]
3 3
¦ I H3 +2 CH3-- C
Al-O-Zr{CH2-C ~>]
O\ CH3 3
There then follows, upon aging, particularly at 50C. and
- 14 -
. . :
-
: 10541S4
above, a parti~l decomposition to form the active catalyst
in which zirconium is at least in part in lower valence
states. This is shown approximately by (C):
''' / '
, O O
\ O
r l~13 1 Al-0\
l1-I3
(C ) ~ / r t C~2~ \ Zr-CH2-C ~>
o L C1~3 . 2 Al-0 C~I3 -~
O\
I ~3~ -
- '~C~I2-C~
. C~3
The neophyl radicals eliminated may either be converted to
t-butyl benzene by picking up a proton from the solvent, or
may couple. Some zirconium may similarly be reduced to
Zr(II) at active polymerization sites, particularly in the
presence of olefin monomers.
In the ethylene polymerization process of this in-
vention when conducted in continuous manner in a stirred
autoclave, the yields obtained have been in excess of
lO,000 parts of polyethylene per part of zirconium when
using the preferred neophyl zirconium aluminate bonded
onto alumina catalyst. Inherently, batch processes are
less efficient but yields in the range of 700-lO00 g. ?
polyethylene per millimole of zirconiu~ p~er hour are
readily obtainable as compared with only 50 to lO0 g.
polyethylene per millimole Zr obtained in a process of
the prior art where there is used as catalyst the reaction
. - 15 -
:
~054154
product of tetra(benzyl) zirconium with hydrated A1203.
In the preferred continuous process, the catalyst
suspension and the ethylene dissolved in an aliphatic or
cycloaliphatic hydrocarbon are each fed continuously to the
~ stirred polymerization zone, the molar ratio of ethylene
- fed to zirconium being maintained at a value in the range of
35,000-400,000 to one.
The polyolefins obtained by the process of this
invention are linear, head-to-tail polymers of high
1~ molecular weight. In the case of ethylene homopolymeriza-
tions, the resultant linear polyethylene has a crystalline
melting point in the range of 133-138C., an annealed -
density in the range of 0.96 to 0.97 g./cm3. If desired,
ethylene polymers of lower density (o.90-0.96 g./cm3) can
be obtained by copolymerization of ethylene with minor
proportions (0.1 to 15 mole%) of higher ~olefins
(preferably C4 to C10) to provide copolymers containing
0.1 to 12 weight % copolymerized higher oleIin using the
process and catalyst of this invention. Such copolymers
contain randomly-distributed side chains of controlled
length which impede somewhat the development of
crystallinity in the solid polymers which are, as a
result, polymers of increased toughness and stress-crack
resistance. As is well known, all of the ethylene
polymers find ~commercial use as self-supporting films,
wire coatings, pipe, and molded articles~of commerce. If
desired, they can be filled with glass or other stiff
fibers, clays and the like to produce hard, sti~f moldings.
The homopolymerization of propylene using the
catalysts of thls invention in the process Or this
,
- 16 -
~054154
invention can be directed, by control of process conditions,
to yield highly stereoregular, head-to-tail crystalline
polypropylene of high molecular weight insoluble in hydro-
carbons at ambient temperatures and sparingly soluble even
at temperatures above 100C. and having a crystalline
melting point in the range of 162-170C., as determined
by either differential thermal analysis or hot-stage
microscope using polarized light, as well as high molecular
weight, linear, head-to-tail polypropylene which is
amorphous, due to atactic steric structure, and soluble
in hydrocarbons even at room temperature. The crystalline
polypropylene has come to be termed, following the
suggestion of Giulio Natta, polypropylene exhibiting
"isotactic" structure due to the presence of long segments
in the macromolecules in which the groups attached to suc-
cessive asymmetric carbon atoms along the chains have the
same configuration. As is well known, crystalline polypro-
pylene finds many commercial uses, particularly as textile
fibers, in both woven and non-woven textiles and as films,
strappings, coatings and molded articles of commerce.
Amorphous polypropylene is useful in blends with crystal-
line polyolefins to provide toughness, and in adhesive
compositions and rubbers.
The catalysts and processes of this invention
can be used to produce amorphous ethylene/propylene
rubbers where from about 30% to about 72~ by weight
(preferably about 50% by weight) of ethylene and,
I correspondingly, 70% to 28% of propylene are combined in
the macromolecules by copolymerization, under constant
environment conditions, of ethylene and propylene. Due
, . .
- 17 -
.
1054~54
to the higher reactivity of ethylene in the polymerization
reaction, a higher proportion of propylene should be used -~
in the monomer feed fed to the polymerization zone than it
is desired to incorporate in the copolymer macromolecules.
If desired to provide ready sites for subsequent
- traditional chemical vulcanizations (cross-linking), minor
proportions of unconjugated dienes (e.g. 1,4-hexadiene,
2-methyl-1,5-hexadiene, etc.) may be included in the co-
polymers by including minor proportions of these diene mono- -
mers in the mixture of monomers fed to the polymerization
zone in the process. Rubbers can also be obtained by the
homopolymerization of conjugated diolefins such as butadiene
or isoprene using the catalysts and process of this inven-
tion. The properties and utilities of these synthetic
rubbers are well known in the rubber industry.
Because the process of this invention uses such
an active and efficient catalyst system, the very low level
of catalyst residues in the polyolefin products produce no
adverse effects on the properties of these polymers.
Therefore, the polymers are used as formed without the
necessity of the expensive and complex catalyst removal
procedures customarily employed in connection with prior
art commercial practice.
The following examples are provided to illustrate
the invention and to provide comparative examples closer to
the more relevant prior art. However, t~e invention is not
to be considered as limited to the particular examples pro-
vided but rather is of the scope hereinabove described.
Example 1. Preparation of Tetra(neophyl) Zirconium.
Magnesium turnings (48.6 g., 2.0 moles) were
'
1054154
charged into a 2-liter, 3-necked glass flask fitted with a
stirrer, N2 inlet, N2 exit connected to a Mineral oil
bubbler, and 500 cc. dropping funnel. The flask was swept
with N2 overnight to remove air and moisture. Then
160 cc. of dry, deoxygenated diethyl ether was added. A
crystal of iodine was added to activate the Mg surface,
and then 11~ g. (0.7 moles) of neophyl chloride dissolved
in 160 cc. of dry toluene was added dropwise. The reaction
mixture was continuously stirred and maintained at
30-35C. until all of the neophyl chloride had been
added. The reaction mixture turned brown during this
period. After one hour a 5 cc. aliquot of the supernatent
solution was removed from the reaction mixture, neutralized
with 20 cc. of 0.1 M aqueous ~Cl and back-titrated to a
pink phenolphthalein end point with 5 cc. of 0.2 M aqueous
NaOH. The concentration of the Grignard reagent was
therefore found to be 2 molar.
The Grignard reagent was transferred to a 2-liter
flask swept with a stream of dry N2. The unreacted Mg was
washed with 400 cc. of dry toluene and the washing added
to the Grignard solution. The Grignard solution (neophyl
magnesium chloride) was cooled to -10C. and then 40 g. of
97% ZrC14 (0.166 moles) was added through a solids
addition tube. The slurry was stirred for 1 hour and
warmed to 50C., then transferred to an inert atmosphere
box and filtered through a l-inch bed of"dried "Celite"
(diatomaceous earth). The filtrate was concentrated by
evaporation. Crystals of solid tetra(neophyl) zirconium
formed upon cooling. The yield of this product was about
70 g. The crystals were purified by recrystallization
-- 19 -- .,
'' ~ ~ ' , . :
: ``
` - 1054i54
from n-hexane. The purified tetra(neophyl) æirconium
product was found to melt at 67-68C. by observation on
a ~isher-Johns hot-stage and 69C. by DSC melting point
deterrrlination in N2. Elemental analysis of this product
; gave C = 75.85%, H = 8.20%; theory for tetra(neophyl)
zirconium, C = 76.99%, H = 8.40%.
Example 2. Preparation of a Neophyl Zirconium Aluminate
on Alumina Catalyst.
; a) Activation of Alumina
111.2 g. of a commercial grade of fumed alumina
having a surface area of 100 m2/g was charged to a vertical
quartz reactor and dried at 1000C. in a stream of flowing
N2 for 6 hours. The dry A1203 was partially rehydrated by
contact with a 50% relative humidity atmosphere at 73F.(23C.)
for 16 hours and then redried to optimum H0-group content
by heating at 4003C. for 4 hours in a stream of flowing N2.
The resultant activated alumina was suspended
under a N2 atmosphere in 1900 cc. of mineral oil containing
100 cc. of petroleum jelly and stored under N2 until used.
A sample of the slurry was ashed and found to contain
0.048 g. alumina per cubic centimeter.
`b) Catalyst Preparation
Ten cubic centimeters of a solution containing
0.074 g. of the tetra(neophyl) zirconium of ~xample 1
dissolved in decahydronaphthalene was added
to 10 cc. of the suspension of alumina in mineral oil with
continuous stirring and this rnixture was allowed to react
at 25C. for 21 hours to provide a suspension of neophyl
zirconium aluminate bonded onto alumina in mineral oil
which was subsequently used to polymerize ethylene. The
- 20 -
1054154
zirconium in this Product was in a reduced state.
Example 3. Polymerization of Ethylene at 150C. Using
Neophyl Zirconium Aluminate on Alumina as
- Catalyst.
A 350 cc. crown-capped bottle was charged with
340 cc. of dry, deoxygenated decahydronaphthalene solvent,
heated to 150C. and the solvent saturated with ethylene
charged at 40 psi. 3.0 cc. of the suspension of neophyl
zir~onium aluminate bonded onto alumina in mineral oil
prepared in Example 2 was then charged into the solution
of ethylene. After 3 minutes, the polymerization was
terminated by the addition of 2 cc. of isopropanol which
reacts to destroy the activity of the catalyst. The
reaction mixture was cooled which caused the polyethylene
to precipitate. The solid polyethylene was isolated by
filtration, washed with cyclohexane and methanol and
dried in a vacuum oven at 80C. for 16 hours. The yield
of solid, dry polyethylene was 0.7 g. Based on this yield,
the rate of polymerization was calculated to have been
780 g/millimole Zr/hr. The solid, linear polyethylene was
white and had a crystalline melting point of 133C., as
determined by DSC technique, and was of high molecular
weight.
Example 4. Polymerization of Ethylene at 80C. Using
Neophyl Zirconium Aluminate on Alumina as
Catalyst.
A 350 cc. crown-capped Pyrex~ bottle containing
200 cc. of dry, deoxygenated toluene maintained at 80C.
was saturated with ethylene at 40 psi. There was then
charged into this solution of ethylene 3.0 cc. of the
suspension in mineral oil of neophyl zirconium aluminate
on alumina, prepared in Example 2. Polymerization
.
- 21 -
~;` ~ 'i
4~54
commenced at once as shown by precipitation of polymer.
Additional ethylene was charged into the reactor to
maintain the pressure at 40 psi. After 1 hour at 80C.,
the polymerization was terminated by the addition of 2 cc.
of isopropanol, and the granular polyethylene ~as recovered
by filtration and dried in a vacuum oven at 80C. for
16 hours. The weight of dry, solid linear polyethylene
recovered was 1.3 g. The polyethylene had a crystalline
melting point of 135C. as determined by DSC techniques
and was of high molecular weight.
Example 5. Polymerization of Ethylene at 80C. Using
Tetra(neophyl? Zirconium as Catalyst. _
A 350 cc. crown-capped bottle was charged with
200 cc. of dry, deoxygenated toluene and saturated at 80C.
with ethylene. A 0.1 M solution in benzene of the tetra-
(neophyl) zirconium of Example 1 was prepared, and 1 cc.
of this solution was charged into the toluene solution of
ethylene. Polymerization comrnenced immediately as shown
by the precipitation of polymer. Additional ethylene was
charged to maintain the pressure at 40 psi. After 1 hour
at 80C., polymerization was terminated by addition of
2 cc. of isopropanol. The solid polyethylene was isolated
by filtration and dried in a vacuum oven for 16 hours at
80C. The weight of the recovered~ dry, solid white
polyethylene was 0.934 g. The polyethylene had a
- crystalline melting point of 135.8C., as determined by
DSC measurement. Based on the yield of polymer, the rate
of polymerization was calculated to have been 9.34 g/milli-
mole Zr/hr. The polyethylene was of high molecular weight.
Example 6. Comparative Activity of Neophyl Zirconium
Aluminate and Benzyl Zirconium Aluminate on
Alumina as Catalysts for the Polymerization
of Ethylene in a_Continuous Process.
- 22 -
: -
~054~54
a) Polymerization of ethylene using neophyl zirconiumaluminate on alumina as catalyst
.
A 0.000625 M solution in n-hexane of the tetra-
(neophyl) zirconium of Example 1 was pr~pared. Using the
process and apparatus diagrammed in Figure I, a suspension
of an active supported catalyst comprising neophyl zirconium
aluminate on alumina is continuously prepared by feeding
the 0.000625 M solution of tetra(neophyl) zirconium from
feed tank, 6, through mixing valve, 15, to premix vessel, 1,
at a rate of 200 cc./hr. and a suspension of activated
alumina, prepared as in Example 2(&), also is fed from
feed tank, 7, through mixing valve, 15, at a rate of 0.5
g. A1203/hr. into premix vessel, 1, a stainless steel,
stirred autoclave of 975 cc. capacity where it is diluted
with 1400 cc. per hour of hexane and maintained at 50~.
Not shown in Figure 1 is a feed tank and line through
which the hexane is fed to premix vessel, 1. After a
hold-up time of approximately 40 minutes, to allow for the
reactions between tetra(neophyl) zirconium and the
activated alumina to produce neophyl zirconium aluminate,
the catalyst suspension is continuously fed to a 265 cc.
second stainless steel autoclave, 2, at the same rate, and
there diluted with 800 cc./hr. of n-hexane while stirring
with mixer, 13. Not shown is a li~e from a hexane feed
tank to autoclave, 2, through which the n-hexane is fed. -
After a hold-up of 6 minutes in the autoclave the diluted
catalyst suspension then is continuously fed through
valve, 16, to a 253 cc. stainless stee~ agitated polymeri-
zation vessel, 3, stirred by mixer, 14, and maintained at
2250 psi and 250C. where it is contacted with ethylene
fed, from reservoir, 9, through valve, 17, as a 7~ weight
- 23 -
1054154
solution in n-hexane, at 200 g. ethylene/hr.
The concentration of the catalyst in the reactor
- with respect to zirconium was 2.0 x 10-5 molar. In order
to control and limit molecular weight o~ the polyethylene,
~2 was also fed to the polymerization vessel at a rate of
100 millimoles/hr. as a 0.0825 M solution in n-hexane.
The H2 tank and feed line are not shown in Figure I; if
desired, this stream can also be fed through mixing valve,
17-
The hold-up time in the polymerization vessel is
maintained at approximately 2.56 minutes by continuously
withdrawing the polymerization mixture through mixing
valve, 19, to a deactivation chamber, a tubu~ar,
turbulent mixer, 4, where the catalyst is deactivated
to terminate the polymerization by addition from reservoir,
12, through mixing valve, 19, o~ a 0.0033 M solution of
isopropanol in n-hexane at a rate of 600 cc./hr to the
reaction mixture containing dissolved polyethylene.
Instead of isopropanol, other alkanols, stearn or CO2, can
be used as the deactivator.
The solution of polyethylene is continuously dis-
charged through an automatic, controlled pressure-reducing
valve, 20, into a product receiver, 5, maintained at 50C.
where the solid polyethylene phase is separated from
solvent; the polymer stream is passed to polymer recovery
system, 11, and recovered from the polyme~ization medium
by filtration, and the polyethylene, wet with n-hexane,
is chopped in a blender, washed with n-hexane and dried
in a vacuum oven at 80C. for 16 hours. Monomers and
solvent recovered from the top of separator, 5, are passed
- 24 _
1054~4
through a refining train, not shown, and then recycled
through mixing valve, 17, to polymerizer, 3.
The rate of polyethylene production during steady-
state operation over a period of several hours was
177 g./hr. (88.5~ cGnversion of the ethylene fed to the
polymeri~er). The yield of polyethylene was 1415 kg./mole
of zirconium. The dried polyethylene had a melt flow, as
determined by ASTM Method 1238-65T, Condition E, of 2.8
decigrams/min. The density of the polyethylene produced,
as determined by ASTM D792-64T (method corrected to 23C.)
was found to be o.960 g./cc. Thus the polyethylene
produced was a highly linear, crystalline polyethylene of
high molecular weight suitable for use in production of
films and ~njection-molded articles, ~;
b) Polymerization of ethylene using benzyl zirconium
aluminate as a catalyst
.
The foregoing experiment (Example 6-a) was
repeated using, however, as a catalyst the reaction product
of the activated alumina and tetra(benzyl) zirconium except
that the concentration of zirconium catalyst was increased
; 20
slightly over that in Example 6(a) to 2.14 x 10 5 molar
in the polymerization autoclave. In this instance the
rate of polyethylene formation was L67 g./hr. (83.8~ con-
version of the ethylene fed).
An analysis of the reactions based on the change
in activity (a) as shown by
where r = hold-up ti~e in the polymerizer
Q = ethylene conversion
- 25 -
~ lOS~lS~
reveals a's of 3.029 min 1 for the neophyl zirconium alumi-
nate catalyst vs. only 2.017 min 1 for the benzyl zirconium
aluminate catalyst. Thus even though the concentration of
neophyl zirconium aluminate catalyst in the polymerizer was
less (2.0 x 10 5 molar) than benzyl zirconium aluminate
~; catalyst (2.14 x 10 5 molar~ the activity of the neophyl
zirconium aluminate was 1.5 times that of benzyl zirconium
- aluminate.
Example 7. Polymerization of Propylene Using Neophyl
Zirconium Aluminate on Alumina as Catalyst
. 10
Into a l-literJ stirred, nitrogen-filled autoclave -
was charged 600 ml of cyclohexane purified by purging with
nitrogen followed by passing it through a bed of acid
alumina under nitrogen. As the autoclave was kept
blanketed with nitrogen 0.2 millimoles of neophyl zirconium
aluminate supported on one gram of fumed alumina, prepared ~ -
as in Example 2, was in~ected by syringe as a slurry in
20 ml of cyclohexane. Propylene was pressured into
20 psi as the system was stirred at ~00 rpm. The tempera~
ture and propylene pressure were raised to 50~60 psi and
maintained at this for 4 hrs. The ten grams of poly-
propylene obtained was in the form of a gel, which was
evaporated to give a tough, flexible sheet. The inherent
viscosity of this polymer was 12.5 dl/100 as measured at
0.1% concentration in decalin at 130C. Thirty-five
percent of the polymer was insoluble in boiling heptane.
The insoluble polypropylene was highly crystalline and
exhibited the isotactic structure. A very tough, rubbery
film 5 mils thick was obtained by compression molding
0.5 g. of the total polymer at 230C., 3000 lbs ram
3
pressure.
- 26 -
~OS4154
Exa~ple 8. Polymerizatiorl of Ethylene with a Neophyl
Zirconium Silicate on Si~ica Catalyst
. . _
20 g. of a commercially available fumed silica
having a surface area of 225 m2/g.was char~ed to a vertical
glass reactor and dried at 200C. in a stream of flowing
nitrogen for 4 hours. One gram of the dried silica was
suspended in 38.5 cubic centimeters of decahydronaphthalene
and 1.5 cc. of 0.2M tetra(neophyl) zirconium in benzene
was added. After 40 minutes the supernatent liquid above
the catalyst was analyzed by gas chromatography. A
material balance showed approximately 2.1 neophyl groups
were displaced from each mole of tetra(neophyl) zirconium
; during formation of the neophyl zirconium silicate on
silica catalyst.
The polymerization of ethylene was brought
about by charging a crown capped bottle containing 340 cc.
of decahydronaphthalene saturated with ethylene at 150C.
and 40 psi with 4 cubic centimeters of the neophyl
zirconium silicate on silica catalyst (0.1 g. silica, 0.03
millimole Zr). After 3 minutes the polymerization was
stopped by addition of 2 cubic centimeters of` isopropanol.
The solution was cooled and the precipitated polymer
separated by filtration, washed with cyclohexane and
methanol, and dried in a vacuum ov~en for 16 hrs. at 80C.
The product recovered, including catalyst residue, weighed
0.345 g. which is equivalent to 0.245 g. of polyethylene.
Based on this yield the rate of polymerization was
calculated to have been 163 g./millimole Zr/hr as contrasted
with the 780 g./millimole Zr/hr achieved in Example 3 by
use of the preferred catalyst of this invention.
- 27 -
... .
..
1054154
,: Example 9. Copolymerization Or Ethylene and Propylene
, with a Neophyl Zirconium Aluminate on
` Alumina Catalyst to for~ a Crystalline
Copolymer.
80 cubic centimeters of deoxygenated hexane in an
agitated vessel was saturated at 25C. with propylene at 20
psi. The pressure was raised to 40 psi with ethylene and
;~ the copolymerization brought about by the addition of 10
cubic centimeters of a neophyl zirconium aluminate catalyst
slurry prepared by reaction of 10 g. of alumina activated
- as in Example 1 and 2.0 millimoles of tetra(neophyl)
-~ zirconium in 210 cubic centimeters of deoxygenated hexane.
After 20 minutes at 25C. the polymerization was stopped
by venting the unreacted olefins. The polymer was
separated by filtration washed with methanol and dried at
80C. for 16 hrs. The product recovered weighed 6.44 g.
This copolyrner had a crystalline melting point of 122.5C.
by DSC techniques and was found to contain 10.1 weight %
copolymerized propylene by infrared analysis.
Example 10. Copolymerization of Ethylene and Propylene
With a Neophyl Zirconium Aluminate on
Alumina Catalyst to Produce an Amorphous
~ 20 Copolymer.
;'''` ' -
2 grams of alumina activated as in Example 1 was
suspended in 40 cubic centimeters of hexane and 2 cubic
centimeters of a 0.2 molar solution of tetra(neophyl) zir-
conium in benzene added. After l hr. a portion of the
slurry was transferred to a vial and the hexane evaporated
under vacuum leaving 1. o6 g. of catalystl The vial was
sealed and placed in a stainless steel-reactor with two
,~ stainless steel balls. The reactor was sealed and charged
.
with 50 g. of propylene, warmed to 25C. and ethylene
added until the pressure in the reactor reached 500 p,i.
':
'' .
r ~ 28 -
.
1054154
:
The catalyst ampoule was broken and the polymerization
allowed to proceed for 1 hr. The amorphous copolymer,
isolated as a rubbery ball, was separated from the glass
and dried to yield 29 g. of copolymer having a copolymer-
ized propylene content of 28.3 weight per cent, as
determined by infrared analysis.
Example 11. Polymerization of 1,3-Butadiene with a
Neophyl Zirconium Aluminate on Alumina
Catalvst
~- A 1 liter agitated flask swept with nitrogen was
charged with 500 cubic centimeters of deoxygenated toluene,
heated to 50C. and saturated with 1,3-butadiene at 2 psi.
Neophyl zirconium alu~inate on alumina catalyst
in hexane, equivalent to 0.38 g. of catalyst (o.076 milli-
moles Zr), was added and the polymerization continued for
1 hr. The product which formed was separated by filtra-
tion, chopped in a blender and dried in a vacuum oven
at 80C. for 16 hrs. The drled product weighed 1.13 g.
which is equivalent to 0.75 g. of polybutadiene. Based
on this yield the rate of polymerization was calculated
to be 9.9 g./millimole Zr/hr. Infrared analysis showed
the structure of the polymer to be of the 1,4-trans-type.
Example 12. Polymerization of Propylene With a Neophyl "
Zirconium Aluminate on Alumina Catalyst
1 gram of alumina activated as in Example 1 was
; suspended in 40 cubic centimeters of dry hexane in a
, . . .
stirred flask under nitrogen. 5 cubic centimeters of
; 0.1 molar tetra(neophyl) zirconium was charged to the
flask. After 16 hrs. the neophyl zirconium aluminate
catalyst was transferred to an ampoule and the hexane
evaporated under high vacuum. The ampoule was sealed
- 29 -
lOS4~5~
and placed in a stainless steel reactor with two stainless
steel balls. The reactor was swept with nitrogen to
exclude all air, sealed, evacuated, cooled and 75 g.
of propylene charged. The reactor was warmed to 50C. -
and the ampoule broken by shaking the reactor. A~ter
1 hour the polymer was isolated, separated from the
glass and dried to yield 26 g. of polypropylene having
a melting point of 158C. and a crystallization point
of 110C. by DSC. The polypropylene had an inherent
viscosity in decahydronaphthalene at 130C. (0.1% solution)
of 9.64. Extraction of the polypropylene with boiling
hexane for 4 hrs. removed 3% of the polymer indicating
the remainder to be substantially high molecular weight
polypropylene of isotactic structure. The hexane
insoluble fraction was further extracted with boiling
toluene. The swollen toluene-insoluble residue, after
drying, had a melting point of 162.5C. by D.S.C., and
amounted to 90% of the or~ginal crude product. The
; insolubility in toluene at the boiling point indicates
that this crystalline polypropylene comprises
macromolecules having substantially completely the
isotactic structure.
Example 13. Terpolymerization of Ethylene, Propylene
and 1,4-Hexadiene with Neophyl Zirconium
; Aluminate on Alumina Catalyst
_ _
4 grams of alumina activated as in Example 1 was
suspended in 80 cubic centimeters of hexane and reacted
with 12 cubic centimeters of a 0.1 molar solution of
tetra(neophyl) zirconium in benzene. A portion of the
slurry was transferred to a glass ampoule and the liquid
evaporated and the catalyst dried under high vacuum. The
- 30 -
iO54154
dry catalyst in the ampoule weighed 1.277 g. The ampoule
was placed in a stainless steel reactor with 2 stainless
steel balls. The reactor was closed and charged with 50
cubic centimeters of l,4-hexadiene and 50 cubic centimeters
of n-hexane. The reactor was cooled, charged wi~h 50 grams
of propylene, warmed to 100C. and pressured to 800 psi
with ethylene. The catalyst ampoule was broken and the
terpolymerization allowed to proceed for 1 hour. The
polymer isolated as a crumb was separated from glass and
10 dried to yield 9 g. of terpolymer. A melt pressed film -
of the terpolymer was analyzed by infrared analysis and -
found to contain 5.5 methyl groups/100 carbons and 8.3
trans-olefin groups/2000 carbons which is equivalent to
15.6% propylene and 2.1~3% hexadiene by weight.
Example 14. Terpolymerization of Ethylene, Propylene and
5-Ethylidene Norbornene with Neophyl Zircon-
_ ium Aluminate on Alumina_Catalyst
0.7353 gram of dry neophyl zirconium aluminate
on alumina catalyst prepared as in Example 13 was sealed
in a glass ampoule. The catalyst ampoule was placed in a
stainless steel reactor with 2 stainless steel balls. The
reactor was closed, charged with 20 cubic centimeters of
5-ethylidene norbornene, cooled, and charged with 75 g. of
propylene. After warming to 100C. the reactor was charged
with 700 psi ethylene and the cataiyst ampoule broken.
After 1 hour the polymer was isolated, separated from glass
iand dried in a vacuum oven at 80C. for 16 hours. A melt-
pressed film of the terpolymer was analyzed by infrared
analysis and found to contain 12 methyl groups/100 carbons
and 4.6 trans-olefinic groups/100 carbons, which is equiva-
lent to a composition of 32 weight % propylene and 1.97
weight % ethylidene norbornene in the terpolymer.
,
- 31 -
: `-
~054~54
Example 15. Copolymerization of Ethylene and l-Octene
~sing Neophyl Zirconium Aluminate on
~lum na Catalyst. _ _
1.12 gram of dry neophyl zirconium aluminate
catalyst prepared as in Example 13 except having a
zireonium content of 0.2 millimoles per gram of alu~ina
was sealed in an ampoule and charged to a stainless steel
reaetor eontaining 2 stainless steel balls. The reaetor
was freed of air and eharged with 10 cubie eentimeters
of l-oetene, warmed to 100C., and pressured with
700 psi of ethylene. The eatalyst vial was broken and
the eopolymerization allowed to proceed for 1 hour.
The product was isolated, separated from glass and
dried. The dry copolymer weighed 3.3 g. and had a
melting point of 120C. as determined on a differential
scanning calorimeter (Du Pont Model 900).
Since the catalysts of this invention are
subject to deactivation by 2~ H20, C02 or other reactive
substances, in all of the examples precautions were
taken to maintain the equipment clean and dry and free
from atmospheric contact, and the solvents, H2 and
. .
monomer were freed from traces of moisture or oxygen
by the use of conventional desiccating agents and
alkali metals.
As shown by the examples, the preferred
eatalyst of this invention has a remarkably high
aetivity as an olefin polymerization catalyst compared
to coordination eatalysts previously known. It has the
further very signifieant advantage that, due to its high
activity, the low coneentration and the innocuous character
of the catalyst residues, which are white, free from
- 32 -
: 105415as
corrosive halogens and non-toxic, it is not necessary
to remove the low level of catalyst residues from the
polyolefins produced. This eliminates the expensive,
time-consuming catalyst-removal process steps
characteristic of previously ~nown commercial processes -
. for the preparation of polyolefins using coordination
catalysts.
The olefin polymers produced by the process of
this invention are regular, linear head-to-tail polymers
of high molecular weight useful for subsequent fabrication
by conventional equipment into tough colorless films,
fibers, molded articles, pipe and wire coatings.
~` V. ANALYTICAL METHODS
(a) The melting points of the polyolefins prepared ---
- were accurately determined by differential thermal analysis
; according to the general method described in khe chapter
"Application of Differential Thermal Analysis to High
Polymers'l, Organic Analysis Volume IV, page 361, Inter-
science Publishers, Inc. (1960). Using a differential
thermal analyzer, e.g., a Du Pont Model 900 DTA, fitted
with a differential scanning calorimeter (DSC) cell
! adjusted to a heating rate of 5C. per minute using an
empty alumlnum pan as a reference, a sample of the polymer
was heated in an aluminum pan to 20C. above its melting
point. The sample was cooled approximately 15 minutes
until it reached a temperature of about 50C. and then
reheated, again at 5C. per minute, and the melting
point observed. This procedure gives comparable melting
points fo~ polyolefins to those obtained by visual
; 30 observation using a hot-stage microscope equipped with
- 33 -
1C~5~5a~
crossed polarizers in accord with the ASTM procedure
Designation D2117-64 for the determination of the melting
point of semicrystalline polymers.
(b) One method for molecular weight determination
is the measurement of inherent viscosity of the polymer
;`- in solution. The measurement of inherent viscosity bears
a direct relationship to the number average molecular
weight for each class of polyolefin and it was used in
the above examples to characterize the polypropylene
products of the examples. The inherent viscosity (~I~
of the polypropylene was measured by dissolving 0.05 g.
of the polyolefin in 50 milliliters of decahydronaphthalene
~' at 170C. The solution was filtered and transferred to an
^ Ostwald viscometer and the viscosity of the polymer
solution and of the decahydronaphthalene solvent measured
at 130C. by noting the time required to pass the same
volume of each material through the viscometer.
The inherent viscosity (~I) was then calculated
by using the following formula:
2.303 log /~low time for soln'n/flow time
~I for solvent7
gm.-of polymer~~n 10~ mL. of s-oIvent.
The inherent viscosity may be correlated with the number
average molecular weight of the linear polyolefin, e.g.,
an inherent viscosity o~ 1.0 corresponds to a number
average molecular weight of 180,000, an ~I of 5 corresponds
- to 750,000 and an ~I of 10 corresponds to 1,800,000 for the
polypropylene polymers disclosed herein.
(c) The weight average molecular weight of the poly-
olefin products herein may be measured by the classical
methods of light scattering. However, in the case of the
,
1054154
linear polyethylene products of the examples, the welght
average molecular weights of the products herein were
determined from a previously-established correlation be-
tween melt flow (ASTM 1238-65T Conditlon E) and weight
average molecula.r weight as determined by light ~catterlng,
e.g., a melt ~low of 1 corresponds to a weight average
molecular weight (~ ) of 140,000 and a melt ~low o~ 3.5 to
~W = 100,000.
(d3 The characterization of tetra(neophyl) zirconium
-10 b~ nuclear magnetic resonance spectroscopy was carried out
according to the general procedure described ~n "Interpre-
;tatlon o~ NMR Spectra" by R. H. Bible, Plenum Press, 1965;
Appendix, page 119. me tetra(neophyl) zirconlum (0.02 g)
was dissolved in 0.2 cc. of deutrobenzene (99.8~) in a
5 mm. O.D. x 5 inch .glass NMR tube, The Rpectrum was
determlned at 42C.
The application is a division of copending appli-
cation Serial No. 227,242, filed May 16, 1975.
- 35 -