~583~5
This invention relates to polytriazines and a process
oE preparing them from polyaromatic cyanates~
This application is divided out of parent application
S.N. 465,260 filed on October 12, 1984. The parent application
relates to the polyaromatic cyanates (and a process for
preparation thereof) mentioned above which can be used to form
the polytriazines of this divisional application.
It is known from German Patent Specification No. 1,190,184
that high molecular weight polytriazines can be obtained by poly-
merizing difunctional or polyfunctional aromatic cyanates atelevated temperature, optionally in the presence of polymerization
promoters. The polymers are characterized for example by their
remarkable stability at elevated temperatures and they are
duroplastic in character after tempering for a sufficiently
long period. The resistance of the polytriazines to acids and
various solvents may also be emphasized.
In addition, it was found by V. V. Korchak et al.
(cf. Vysokomolekulyarnye Soedineniya 1974, number 1, pages 15 to
21) that the thermal and thermo-oxidative destruction of poly-
~0 triazines based on aromatic cyanates is greatly influenced bymoisture.
Finally, it is known from German Patent 1,720,740
that polyfunctional aromatic cyanates can be combined with
powder-form and/or fibrous fillers or reinforcing materials and
subjected either to a preliminary or subse~uent heat treatment at
about 5QC to 150C, the resultlng molding composition molded and
hardened at temperatures in the range from about 150C to 250C.
~ !
-- 1 --
~Z~8345
In mar}y cases the resulting moldings also show
inadequate thermal stability after storage in a moist, tropical
atmosphere.
Polyaromatic cyanates which prepare polytriazines which
are hydrolytically stable are needed. Polyaroma-tic cyanates which
are useful in preparing polyaromatic triazines which are thermally
stable are further needed.
The invention of the parent application is directed to
a polyaromatic cyanate characterized by having the formula
`'10
(,D)t ~ t (,)t (,)t(D)t
(NCO~q Ar --- B Ar _ B Ar ~OCN)S
(OCN)r
wherein:
Ar is an aromatic radical;
B is a C7 20 polycyclic aliphatic radical;
D is any nonactive hydrogen-containing substituent;
q, r and s are independently in each occurrence the
integers 0, 1, 2 or 3; with the proviso that the sum
of q, r and s is greater than or equal to 2;
t is independently in each occurrence an integer of
between 0 and ~; and
x is a number between 0 and 5.
Another aspect of the invention of the parent application
is a process for the preparation of the polyaromatic cyanates.
This process is characterized by first preparing cyanogen chloride
in situ by contacting a solution of chlorine in a chlorinated
-- 2 --
~Z5~33~5
hydrocarbon with an aqueous solution of alkali metal cyanide.
Then the aqueous layer contianing the alkali metal chloride by-
product is separated from the chlorinated hydrocarbon layer con-
taining the cyanogen chloride. Then a solution of a polycyclic
bridged hydroxy-substituted polyaromatic phenol in a suitable
solvent is contacted with the cyanogen chloride solution in the
presence of a tertiary amine to prepare the polyaromatic cyanates
of this invention.
One aspect of the present invention is a polytriazine
characterized as being the reaction product of (a) between 1 and
100 mole percent of the polyaromatic cyanate ester of this
invention and (b) between Q and 99 mole percent of one or more
cyanate-containing compounds known in the art as useful for the
preparation of polytriazines.
According to another aspect of the present application
there is provided a process for preparing the polytriazines
which comprises reacting between 1 and 100 mole percent of the
above polyaromatic cyanate with between 0 and 99 mole percent
of the above cyanate-containing compound.
The novel polyaromatic cyanates prepare polytriazines
which are surprisingly more stable to hydrolysis than prior art
polytriazines.
The polytriazines of this invention can be used as
cure-in-place resins or fabricated in the form
~4~ ~S~3~5
of shaped articles, where thermal stability, chemical
inertnèss and solvent resistance are desirable or
required.
Aromatic radical, Ar, refers herein to any
radical containing an aromatic group. Examples of
aromatic radicals include benzene, naphthalene,
phenanthracene, anthracene, or biaromatic radicals, or
two or more aromatic radicals bridged by alkylene
moieties. Ar is preferably a benzene, naphthalene,
biphenyl, benaphthyl, or a diphenylalkylene radical.
Ar is more preferably a benzene radical.
Polycyclic aliphatic radical re~ers herein to
any aliphatic radical which contains two or more cyclic
rings. The polycyclic aliphatic radicals may contain
one or more double or triple bonds. Preferred polycyclic
aliphatic radicals correspond to the formulas
II, -CH2 ~ CH2- III,
~ IV, -CH2 ~ D
D
-CH2 ~ CH2- VII, ~ , VIII, ~ IX,
31,877-F -4-
,4~f~L
345
~ X, ~ C1 XI, ~ XII and
~ XIII,
wherein:
O O
,. ..
Y is -CH2, -S-, -S- or -S- ;
1 0 0
and D is C1 ~ alkyl.
B is more preferably a radical which corre-
sponds to one of the formulas II, III, IV, V, VI, VII,
VIII or XIII with radicals corresponding to formulas
II, III, IV, V or XIII being even more preferred, and
radicals corresponding to formula II being most preferred.
D is any substituent which can be substituted
on an organic hydrocarbon radical, with the exception
that the substituent cannot contain an active hydrogen
atom. Substituents within the scope of this invention
are well-known to those skilled in the art. Active
hydrogen atom means herein a hydrogen atom which is
bonded to an oxygen, sulfur or nitrogen atom. Examples
of substituents within the scope of D include alkyl,
alkenyl, alkynyl, aryl, alkaryl aralkyl, halo, alkoxy,
31,877-F -5-
8345
nitro, carboxylate, sulfone, sul~ide or carbonate
moieties. Preferred substituents are Cl l0 alkyl,
Cl lO alkenyl, nitro, and halo moieties, ~7ith C'l 3
alkyl, Cl 3 alkynyl, bromo and chloro moieties being
most preferred.
Preferably, ~, r and s are independently l or
2, and are most preferably l. Preferably, t is indepen-
dently an integer of 0, l or 2, more preferably O or l,
and most preferably 0. Preferably, x is between 0 and
2 inclusive, and more preferably between 0 and l inclusive.
The polyaromatic cyanates
usually exist as a mixture of many isomers. Further,
these polyaromatic cyanates usually are found as a mix-
ture of compounds in which x is between O and 5. Usu-
ally the number given for x in a particular mixture isan average number.
In one preferred embodiment the polyaromatic
cyanates correspond to the formula
OCN
20 NCO ~ ~ ~ OCN
whexein x is a real number of between 0 and 5, inclusive.
The polyaromatic cyanate esters
are generally prepared by contacting a suitable
polyaromatic phenol with cyanogen chloride, in the
31,877-F -6-
l~S~3~5
presence of a tertiary amine. It 1s preferable to
prepare the cyanogen chloride in situ by contacting a
solution of chlorine in a chlorinated hydrocarbon
solvent ~ith an aqueous solution of an alkali metal
cyanide. The reaction mixture separates into an organic
layer of the chlorinated hydrocarbon containing the
cyanogen chloride and an aqueous layer containing the
alkali metal chloride salt. Generally, the alkali
metal cyanide and chlorine are reacted in a molar ratio
10 of between 1.0:1.0 and 1.0:1.15, preferably between
1.0:1.0 and i.0:1.05; and most preferably 1.0:1Ø An
excess of either may result in undesirable conseguences,
that is, excess chlorine may later react with the
phenol, and excess alkali metal cyanid0 may result in a
lower product purity. This contac-ting is done at a
temperature of 0C or below, preferably less than
-15C. Above 0C the cyanogen chloride will ~rimerize.
Preferable solvents for the chlorine are the aliphatic
chlorinated hydrocarbons, such as, for example, methyl
chloride, chloroform, and 1,1,1-trichloroethane. The
preferred alkali metal cyanide is sodium cyanide.
The aqueous layer and organic layer are then
separated. The separation of the organic layer from
the aqueous layer is advantageous as the presence of
the agueous layer in further processing adversely
affects the purity of the polyaromatic cyanates
eventually prepared.
The organic layer containing the cyanogen
chloride is then contacted with a polycyclic bridged
hydroxy-substituted polyaromatic compound dissolved in
a suitable solvent in the presence of a tertiary amine.
31,877-F -7-
~5~33~5
Polycyclic bridged hydroxy-substituted poly-
aromatic compounds useful in this process correspond to
the formula
( )t r (D~t (D)t ~ (D)t (D)t
(HO~q Ar _ _ B _ Ar ¦ B - Ar ~OH)s
(OH)r lX
wherein Ar, B, D, q, r, s, t and x are as deflned
hereinbefore.
In one preferred embodiment the polycyclic
bridged hydroxy-substituted polyaromatic compounds cor-
respond to the formula
OH
HO ~ ~ ~ ~ _ ~ OH
wherein x is as defined hereinbefore. The polycyclic
bridged hydroxy-substituted polyaromatic compounds used
usually exist as a mixture of isomers. Further, the
polycy~lic bridged hydroxy-substituted polyaromatic
compounds are found as a mixture of compounds in which
x is between 0 and 5. Usually the number given for x
is an average number. The solvents used for the
polycyclic bridged hydroxy-substituted polyaromatic
compounds are secondary alcohols, tertiary alcohols, or
chlorinated hydrocarbons. Preferred solvents are
secondary alcohols or aliphatic chlorinated hydrocarbons,
with isopropyl alcohol and methylene chloride most
preferred.
31,877-F -8-
~ZS839~5
The process is preferably done at a tempera-
ture of 0C or below, more preferably -15C or below.
For complete conversion of the hydroxy rnoi-
eties on the aromatic radicals to cyanate moieties, at
least 1 mole of cyanogen chloride for each hydroxy
equivalent is needed. It is preferable to use an
excess of lO mole percent of cyanogen chloride for each
hydroxy equivalent to insure complete conversion.
The tertiary amine acts as a hydrochloride
acceptor, and as a result a tertiary amine hydrochlorlde
salt is a by-product of the process. Generally, at
least one mole of tertiary amine for each hydroxy
equivalent is used. ~ydroxy equivalent refers herein
to the average molecular weight of the polycyclic
bridged hydroxy-substituted polyaromatic compound
divided by the average number of hydroxy moieties per
molecule.
The polyaromatic cyanates can be recovered
` from the reaction solution in the ~ollowing manner.
The reaction mixture is first contacted wi-th a dilute
agueous solution of base, such as a bicarbonate, to
remove the excess cyanogen chloride~ Then the reaction
mixture is contacted with water to remove the tertiary
amine hydrogen chloride salt. Thereafter, the reaction
solution is contacted with a dilute a~ueous acid solution
to neutralize any base present. A 1-20 weight percent
solution of hydrochloride, phosphoric or sulfuric acid
can be used, preferably a 5-10 weight percent solution.
The reaction solution is then contacted with water to
remove any impurities which may be present. The reaction
solution is dried over a dessicant to remove the water,
and the solvent is stripped off.
31,877-F -9-
-~S~33~5
The polyaromatic cyanate recovered is of sur-
prisingly high purity and can be used directly to
prepare polytriazines.
.,
Suitable pol~cyclic bridged hydroxy-
substituted compounds can be
prepared by reacting an arornatic compound, containing
at least one aromatic hydroxy moiety and one position
on the aromatic ring which can be alkylated, with an
unsaturated polycyclic aliphatic compound under conditions
such that a suitable polycyclic bridged hydroxy-
substituted polyaromatic compound is
prepared.
Suitable substituted aromatic hydroxy com-
pounds which can be employed herein include any such
compounds which contain one or two aromatic rings, at
least one phenolic hydroxyl group and at least one
ortho or para ring position with respect to a hydroxyl
group available for alkylation.
Particularly suitable hydroxy-substituted
aromatic compounds which can be employed herein include,
for example, phenol, chlorophenol, bromophenol, methyl-
phenol, hydroquinone, catechol, resorcinol, guaiacol,
pyrogallol, phloroglucinol, isopropylphenol, ethylphenol,
propylphenol, t-butylphenol, isobutylphenol, octylphenol,
nonylphenol, cum.ylphenol, p-phenylphenol, o-phenylphenol,
m-phenylphenol, bisphenol A, dihydroxydiphenyl sulfone,
or mixtures thereof.
The hydroxy-substituted polyaromatic compound
is contacted with the unsaturated polycyclic aliphatic
compound optionally in the presence of a solvent.
31,877-F -10-
5~ 5
Prefexred solvents include c~l1orinated hydrocarbons,
aliphatic hydrocarbons, aromatic hydrocarbons and
nitro-substituted hydroc~rbons. In general the hydroxy-
-substituted polyaromati~ compound is contacted wlth
the unsaturated polycyclic aliphatic compound in a mole
ratio of between 20.0:1.0 and 1.0:1.0, preferably
between 10.0:1.0 and 1.5:1Ø
These reactants are preferably contacted in
the presence of a catalyst.
Acid catalysts which can be employed herein
include, for example, Lewis acids, alkyl, aryl and
aralkyl sulfonic acids, and disulfonic acids of diphenyl-
oxide and alkylated diphenyloxide, sulfuric acid, or
mixtures thereof. Preferable catalysts are such Lewis
acids as BF3 gas, organic complexes of boron trifluoride
such as those complexes formed with phenol, cresol,
ethanol, or acetic acid. Also Lewis acids include, for
example, aluminum chloride, zinc chloride, or stannic
chloride. Also catalys~s include, for example, activated
clays, silica, or silica-alumina complexes.
In preparing the compounds which contain an
average of more than one phenolic hydroxyl group and
more than one aromatic ring per molecule, the reaction
between khe phenolic hydroxyl-containing compounds and
the unsaturated hydrocarbons can be conducted at temper-
atures of from 33C to 270C, preferably from 33C to
210C.
The polyaromatic cyanates
are useful in preparing polytriazines. The polytria-
. 30 zines of this invention comprise the reaction product
. . .
`` 31, 877-F -11- .
~S~34~5
of (a) between 1 and 100 percent by weight of the
polyaromatic cyanate of this invention, an~ (b~ between
0 and 99 percent by weight of a cyanate which is useful
for preparing triazines, such cyanates being well-known
to those skilled in the art.Suitable prior art
cyanates include those corresponding to
: the formula Ar~OCN) wherein Ar is an arornatic radical,
and n is an integer of from 1 to 5. Preferable cyanates
include those corresponding to the formula
. ( )b (R') e
- wherein
each R is the same or different and repre-
~ 15 sents hydrogen, halogen, straight and branched
` Cl-C20 alkyl, phenyl, alkoxy radicals having from
1 to 4 carbon atoms, alkoxy carbonyl radicals hav-
ing from 1 to 4 carbon atoms in the alkyl group;
or two adjacent radicals R on the same nucleus may
together form a carbocyclic 5- or 6-membered ring,
two adjacent radicals R may, together with a
hetero atom (O, S, N), form a 5- or 6-membered
heterocyclic ring,
R' has the same meaning as R or represents
the group
31,877-F 12-
`; '
~25~33~5
-A~(OCN)d
(R)b
A represents a direct bond, a C1-C20 alkylene
group optionally substituted by C1-C4 alkyl or
phenyl, a cycloaliphatic or aromatic 5- or
6-membered ring optionally interrupted by oxygen,
a sulfonyl group (-S02-~, a carbonyl dioxide
group,
(--OCO--).
O
or a carbonyl group;
a represents a number of from 1 to 5 when
e21, and a number of from 2 to 5 when e=0;
b represents 5-a when e21 and 6-(a+d) when
e=0;
c repre~ents 5-d;
d represents a number of from 0 to 5, and
e represents 0, 1, 2 or 3,
with a proviso that the sum of a and d is always a
number from 2 to 5.
The following compounds are specifically
mentioned as examples of conven-tional cyanates within
one or more of the formulas noted above: 1,3- and
1,4~dicyanatobenzene, 2-tert-butyl-1,4-dicyanatobenzene,
31,877-F -13-
:~Z583~
2,4-dimethyl-1,3-dicyanatobenzene, 2,5-di-tert-butyl-
-1,4-dicyanatobenzene, tetramethyl-1,4-dicyanatobenzene,
2, 4, 6-trimethyl-1,3-dicyanatobenzene, 4-chloro-1,3-dicya-
natobenzene, 1,3-, 1,4-, 1,5-, 1,6-, 1,7-, 1,~-, 2,6 or
2,7-dicyanatonaphthalene, 1,3,5-tricyana-tobenzene; 4,4'-di-
cyanatodiphenyl, 2,2'-dicyanatodiphenyl, 3,3',5,5'-tetra-
methyl-4,4'-dicyanatodiphenyl, 3,3',5,5'-tetrachloro-4,4'-
-dicyanatodiphenyl, 3,3',5,5'-tetrachloro-2,2'-dicyanato-
diphenyl, 2,2',6,6'-tetrachloro-4,4'-dicyanatodiphenyl,
4,4'-bis-[(3-cyanato)-phenoxy]-diphenyl, 4,4'-bis-[(4-cy-
anato)-phenoxy]-diphenyl; 2,2'-dicyanato-1,1'-binaphthyl;
4,4'-dicyanatodiphenyl ether, 3,3',5,5'-tetramethyl-4,4'-
-dicyanatodiphenyl ether, 3,3',5,5' tetrachloro-4,4'-di-
cyanatodiphenyl ether, 4,4'-bis-[p-cyanatophenoxy]-diphe-
nyl ether, 4,4'-bis~[p-cyanatophenylisopropyl]-diphenyl
ether, 4,4'-bis-[p-cyanatophenoxy] benzene, 4,4'-bis-[m-
-cyanatophenoxy]-diphenyl ether, 4,4'-bis-[4-(4-cyanato-
phenoxy)-phenyl sulfone]-diphenyl ether; 4,4'-dicyanato-
diphenyl sulfone, 3,3',5,5'-tetramethyl-4,4'-dicyanato-
20 diphenyl sulfone, 3,3',5,5'-tetrachloro-4,4'-dicyanato-
diphenyl sulfone, 4,4'-bis-[p-cyanatophenylisopropyl]-
-diphenyl sulfone, 4,4'-bis-[(4-cyanato)-phenoxy]-diphe-
nyl sulfone, 4,4'-bis-[(3-cyanato)-phenoxy]-diphenyl sul-
fone, 4,4'-bis-[4-(4-cyanatophenylisopropyl)-phenoxy]-
-diphenyl sulfone, 4,4'-bis-[4-cyanatophenyl sulfone)-
-phenoxy]-diphenyl sulfone, 4,4'-bis-[4-(4-cyanato)-di-
phenoxy]-diphenyl sulfone, 4,4' dicyanatodiphenyl meth-
ane, 4,4'-bis-[p-cyanatophenyl]-diphenyl methane, 2,2-
~bis-(p-cyanatophenyl)-propane, 2,2-bis-(3,5-dimethyl-
30 -4-cyanatophenyl)-propane, 2,2-bis-(3,5-dichloro-4-cya-
natophenyl)-propane, 1,1-bis-[p-cyanatophenyl]-cyclohex-
ane, bis-[2-cyanato-1-naphthyl]-methane, 1,2-bis-[p-cya-
natophenyl]-1,1,2,2-tetramethyl ethane, 4,4l-dicyanato-
benzophenone, 4,4'-bls-(4-cyanato)-phenoxybenzophenone,
31,877-F -14-
~S83~5
1,4-bis-[p-cyanatophenylisopropyl]-benzene, 2,2',5,5'-
-tetracyanatodiphenyl sulfone; polycyarlic acid esters of
novolaks (reaction products of phenol or alkyl- or
halogen-substituted phenols.with formaldehyde in acid
5 solution) having from 3 to 5 OCN groups and the like.
Preferred conventional cyanate containing compounds
include 2,2-bis~p-cyanatophenyl)-propane and 2,3-bis-
(3,5-dibromo-4-cyanatophe.nyl)-propane.
The polytriazines of this inventio~ prefer-
ably comprise the reaction product of (a) between 25
and 100 percent by weight of the polyaromatic cyanatesand (bi between 0 and 75 percent by
weight of a cyanate which is useful in preparing polytri-
azines. More preferably, the polytriazines of this
invention comprise the reaction product (a) ~e-tween 50
and 100 percent by weight of the polyaromatic cyanate
and (b) between 0 and 50 percent by
weight of a cyanate useful in preparing polytriazines.
i The prior art cyanates may comprise mono-, di- and
polycyanates.
The polytriazines of this invention may com-
prise up to 30 percent of monocyanate compounds, for
example, Ar~OCN)n wherein n=1. The use of monocyanates
give the polytriazines modified properties, for example,
solubility, glass transition temperature, moisture
resistance and impact resistance.
Thè formation of polytriazines arise from the
cyclotrimerization of aryl cyanates to prepare 1,3,5-tri-
aryloxytriazines. The use of the difunctional and
polyfunctional polyaromatic cyanates
31,877-F -15-
;~5~33~S
in the cyclotrimerization process results in the prepara-
tion of a three dimensional network polymer which is
hard, infusible and insoluble.
- The term polytriazines as used herein
refer to both fully cure~ polytriazine polymers,
and partially cured polytriazine prepolymers. Fully
cured polytriazines are essentially free of cyanate
functionalities. The prepolymers are cyanate group-
-containing polytriazines oE liquid, wax-like or solid
consistency and are soluble in organic solvents. These
prepolymers are highly stable in storage. These
prepolymers may be later converted to high molecular
weight polytriazines when exposed to polymeriza-tion
conditions. Prepolymers are prepared to permit easy
handling o~ a resin prior to final use. Further, these
prepolymers are useful in the production of coatings on
such substrates as metals, cermics, glass and earthenware,
and as impregnating lacquers or laminating resins.
In the preparation of the polytriazines, aro-
matic polycyanates are contacted in the presence of acatalyst at a temperature of between 20c and 200c,
optionally in the presence of a solvent. Preferable
temperatures are between 80C and 180C. The prepoly-
mers are prepared by the same process, except either a
lower temperature or a lower amount of catalyst is
used, so that the aromatic polycyanates do not completely
polymerize.
The rate of polymerization is dependent upon
the temperature and the catalyst amount. As either, or
both, increase, the rate of polymexization increases.
At higher temperatures, a lower amount of catalyst is
31,877-F -16-
~i83~5
.,
.
necessary for the desired amount of polymerization than
is necessary at lower temperatures.
.
Useful catalysts include acids, bases, salts,
nitrogen and phosphorus compounds, for example, Lewis
5 acids such as AlC13, BF3, FeCl3, TiC14, ZnCl2, SnCl4;
proton acids such as HCl, H3PO4; aromatic hydroxy com-
pounds such as phenol, p~nitrophenol, pyrocatechol,
dihydroxy naphthalene, sodium hydroxide, sodium methylate,
sodium phenolate, trimethylamine, triethylamine, tribu-
tylamine, diazobicyclo-(2,2,2)-octane, quinoline, iso-
quinoline, tetrahydroisoquinoline, tetraethyl ammonium
chloride, pyridine-N-oxide, tributylphosphine, phospho-
line-~3-l-oxa-l-phenyl, zinc octoate, tin octoate, zinc
naphthenate, cobalt salts of C6 20 carboxylic acids and
mixtures thereof. Prefe-rable catalysts are the cobalt
- salts of C6 20 carboxylic acids, with cobalt naphthenate
and cobalt octoate being most preferred.
Generally, any amount of catalyst which cata-
lyzes the preparation of polytriazines is suitable.
Preferably, between 0.001 and 10 percent by weight of
the cyanates of catalyst is used.
Solvents can be any
compound which dissolves the aromatic polycyanates and
does not interfere with the reaction. Suitable solvents
include aromatic hydrocarbons, alcohols and ketones.
The polyfunctional aromatic polycyanates may
be combined with the powder-form or fibrous fillers or
reinforcing materials either before or af-ter heat
treatment of the aromatic polycyanates and by basically
30- any method. For example it is possible to impregnate
31,877-F -17-
~5~3345
powder-form or fibrous fillers or reinforcing materials
such as quartz sand or glass cloths, with the aromatic
cyanates, optionally in solution. Examples of the
solvents which may be used for this purpose and which,
generally, have to be removed again afterwards, are
inert solvents such as methylene chloride, acetone,
methylethyl ketone, xylene, ethyl acetate benzene,
toluene, tetrahydrofuran, chlorobenzene, dibutyl ether,
dimethyl formamide and tetramethylene sulfone.
Suitable fillers and reinforcing materials
are, generally, in any powder form and/or fibrous prod-
ucts, for e~ample, of the type commonly used in the
production of moldings based on unsaturated polyester
resins or epoxide resins. Examples of products such as
these are, primarily, granular fillers such as quartz
powder, ground shale, asbestos powder, powdered corundum,
chalk, iron powder, aluminum powder, sand, or gravel,
also inorganic or organic fibers, more especiall~ glass
fibers in the usual textile forms of fibers, filaments,
rovings, yarns, nonwovens, mats or cloths. In this
connection, amino silane-based finishes have proven to
be particularly effective. It is also possible to use
corresponding textile structures of organic, preferably
synthetic fibers (polyamides, polyesters) or on the
basis of quartz, carbon, metals, etc., as well as
monocrystals (whiskers).
The end products combined with fillers or
reinforcing materials may be used in particular in ves-
sel and pipe construction by the winding technique, in
electrical engineering, in mold construction and tool
making and also in the construction of heavily stressed
components, in the lightweight construction of vehicles
in aeronautical and astronautical engineering.
31,877-F -18-
~5B345
The followlng examples are included for
illustrative purposes only, and are not intended to
limit the scope of the invention or claims.
Example 1
Polytriazine castings of each of the following
cyanate~containing compounds are prepared.
OCN
Nco~
NCo ~ C
and
CH3 ~ 3 III
CH3 3
wherein formula I is an example of the invention of the
parent application and formulas II and III are not.
The polytriazine castings of the aromatic
cyanates df formulas I and II are prepared by heating
31,877-F -19-
~583~5
about 6 g of the respective cyanate along with about
200 parts per million of cobalt naphthenate at 150C
for l hour and 20 minutes and then at 200C for 3
hours.
The castings of formula III are prepared by
heating about 6 g of formula III along with 200 parts
per million of cobalt naphthenate at 180C for 2 hours
and 250C for 90 minutes.
All of the castings are monitored by differ-
ential scanning calorimetry to insure the castings have
no uncured cyanate functionalities.
A casting of each of the polytriazines is
exposed to the following test conditions. In Test 1,
the castings are boiled in water for 96 hours. In Test
lS 2, the castings are immersed in 20 weight percent
hydrochloric acid for 2.5 hours at room temperature and
then at reflux for 4.5 hours. In Test 3, the castings
are immersed in 40 weight percent sodium hydroxide at
room temperature for 2.5 hours, then at reflux for 4.5
hours.
Each casting is weighed before and after each
test. Table I compiles the test resul-ts.
TABLE I
___Weight Change (~)
25 Test Cyanate ICyanate IICYana-te III
1 +0.63 + 1.08 +1.26
2 +0.26 - 4.35 -~1.55
3 -1.69 -28.68 -5.78
31,877-F -20-
~5~3B~
The weight gains are due to the adsorption of
water by the samples. The weight losses are due to the
decomposition of the polymer due to hydrolysis. Generally,
water is adsorbed by the pol~mer prior to hydrolysis.
The example demonstrates that the polytria-
zine prepared from the compound corresponding to formula
I is significantly more resistant to hydrolysis than
the polytriazines prepared from compounds corresponding
to formula II or III. Visual lnspection of the castings
after Test 2 shows that the casting prepared from the
compound corresponding to formula I has no change in
appearance, whereas the casting prepared from the
compound corresponding to formula II has lost lts
transparency due to surface pitting. A visual inspection`
lS after Test 3 of the casting prepared from the compound
corresponding to formula I shows slight surface pitting,
whereas a visual inspection of the castings prepared
from the compound corresponding to formula II after
Test 3 shows the casting to have numerous voids throughout
and that the casting readily crumbles under physical
stress.
Example 2
An 85 percent solution of polyaromatic cya-
nate I in me-thyl isobutyl ketone containing 0.016
weight percent of cobalt naphthenate are used to
impregnate fiberglass cloth. Eight plys of the
impregnated cloth are laid up and cured in a press at
175C and 300 psi (2.07 MPa) for 1 hour to give a 0.062
inch (1.57 mm) thick laminate which has a glass transi-
tion temperature of 265C. The laminate shows a 0.09percent by weight absorption of water after boiling for
an hour at 15 psi.
31,877-F -21-
583~5
Example 3
A 50 percent solution of a pol~aromatic cya-
nate corresponding to the formula
OCN1
S NCO ~ ~3_OCN IV
2 . 0
in methyl ethyl ketone containing 0. 02 percent of
cobalt octoate is used to impregnate fiberglass cloth,
six plys of which are laid up and cured in a press at
175C and 300 psi (2.07 MPa) for 1 hour. A laminate
using the polyaromatic cyanate of formula II (not an
example of the invention) is prepared in the same
manner. Both laminates are subjected to humidity aging
at 71C for 1000 hours at 100 percent humidity. The
laminate prepared from formula IV shows water absorption
of 0.59 percent, while the laminate prepared from
formula II absorbs 0.83 percent water (the experimental
error is 0.01 percent). This example demonstrates that
the polytriazines prepared according to this invention
absorb signifi.cantly less water than polytriazines
prepared from prior art cyanates.
!
Example 4
A fiberglass cloth laminate is prepared from
a 50 percent solution of formula IV in methyl ethyl
ketone without catalyst. The laminate is heated at
150C for 15 minutes, and then inserted into a 215C
press at contact pressure. The temperature is raised
31,877-F -22-
;`
~;~S~33a~5
to 250C over a period of 8 minutes and a pressure of
100 psi (O.689 MPa) is then applled. After ~5 minutes,
the laminate is removed and post-cured for 1 hour at
250C and then ~or 1 hour at 275C. The 1aminates are
of an E glass Style 7781, A 1100 Finish, 6-ply and 27
percent resin.
The laminate is divided into different por-
tions and several tests are run. In the control, the
flexural strength and flexural modulus are determined
10 at room temperatures (23C) and 190C. This testing is
done in accordance with ASTM D-790. Other portions of
the laminate are exposed to different conditions and
thereafter the flexural strength and flexural modulus
are teste~.
In Test 4 the laminate is exposed to air at
200C for 500 hours. In I'est 5 the laminate is exposed
to 100 percent humidity at 50C for 570 hours. In Test
6 the laminate is immersed in CH2Cl2 for 7 days. In
, Test 7 the laminate is immersed in methanol for 7 days.
In Test 8 the laminate is immersed in toluene for 7
days. The percentage of the flexural strength and
modulus of each laminate compared to the control at
room temperature is calculated. The laminates are also
weighed before and after each treatment and the percent
change relative to the standard is calculated. The
results are compiled in Table II~
Table II demonstrates that glass laminates
prepared using the polyaromatic cyanates of the
invention o the parent application are stable to heat,
humidity and contact with common solvents such as
methanol and toluene.
31,~77-F -23-
~S~33~S
0 ~ ~
o~ ~ o o a~
o~n
U~ ~1
_ _ _
r~ ,1 (d~ o t~ N
~ o ~n ~4
O _ r~) N O t~
~1
~ aJ ~ U~
X ~O ~ I o ~1 ~D O O
~-1 ~,,a
O
o a
_ _
~: ~ ~ N ~ ~ N ~Y) N
a~ ~ o ~ o
O Ul ~ . ,~ ~ N
~1 ~4 ~ ~ N t~) N ~ N N ~I N N
_ _ _ _ _ ~ _
h
O
O ~ ~ 0 CO
Val
H O~! ~)
~_~ O U~
~ ~ _
O-- ~ _~ _
~¢ a) o u~ p~. L~ O
~D 11') CO O ~ IJ) I I I
_ ~ d~
-~
~ ~o a O ~ N O d~
~1 ~ ~1 I C~ O ~ O
1:4 O ~1 ;~ ~ ~ ,1
o a~
U)-- ~
o o
~) O U~ O ~ ~ ~N 0 ~1 0 ~ ~ ~ O
,~ ~ N ~ 111 ~ N
~ a
0 F~ I O O N O O
3V I + + + +
~a
a
U~
o) ~ .
~ ~n . .
3 1, 8 77 -F . -24-