PLASTIC FILM
This application is a divisional application of Canadian patent Application
no.
2,390,307 filed on October 26, 2000.
The invention concerns a plastic sheeting with a rough surface to increase the
coefficient o-f friction.
Such shc;eting is known in practice, whereby a granular fillei- is usually ali-
eady
inixed into the plastic.
Howevei-, this causes the sheeting itself to be equipped with only liniited
strength
and the roughness is also low.
It is the task of the invention to develop a sheeting of the said type in such
a way
as to achieve a very good surface roughness without impairing the strength of
the
sheeting.
CA 02597766 2007-08-31
2
This task is solved accot-ding to the invention in that at least one siLie of
the
sheeting is equipped witli a layei- containing the rough surface.
ONvin~, to the separation of the cari-ier layer and the layei- with a rough
surface,
both can be optimally designed.
It has proved extremely advantageous if, according to an advantaQeous
embodiment of the invention, the actual sheeting and the layei- ot- layers
equipped
with the rough surface are produced by the coextnision process.
A rational production of the sheeting is thereby guaranteed despite the
separate
effects on the layers.
According to the present invention, there is provided a use of a plastic
sheeting
to cover a viscous surface, wherein
the plastic sheeting comprises at least one side with at least one layer which
contains a rough surface to increase a coefficient of friction thereof;
the plastic sheeting and the at least one layer with the rough surface is
produced
by a coextrusion process; and
the at least one layer with the rough surface is formed in the plastic
sheeting by
a dissolved propellant which generates gas bubbles immediately after leaving a
coextrusion nozzle, the gas bubbles despoiling the at least one layer in such
a
way that an irregularly rough surface is produced.
According to the present invention, there is also provided use of a plastic
sheeting to cover a roof surface, wherein
the plastic sheeting comprises at least one side with at least one layer which
contains a rough surface to increase a coefficient of friction thereof;
the plastic sheeting and the at least one layer with the rough surface is
produced
by a coextrusion process; and
CA 02597766 2007-08-31
2a
the at least one layer with the rough surface is formed in the plastic
sheeting by
a dissolved propellant which generates gas bubbles immediately after leaving a
coextrusion nozzle, the gas bubbles despoiling the at least one layer in such
a
way that an irregularly rough surface is produced.
According to the present invention, there is also provided a use of a plastic
sheeting to cover timber boarding, wherein
the plastic sheeting comprises at least one side with at least one layer which
contains a rough surface to increase a coefficient of friction thereof;
the plastic sheeting and the at least one layer with the rough surface is
produced
by a coextrusion process; and
the at least one layer with the rough surface is formed in the plastic
sheeting by
a dissolved propellant which generates gas bubbles immediately after leaving a
coextrusion nozzle, the gas bubbles despoiling the at least one layer in such
a
way that an irregularly rough surface is produced.
According to the present invention, there is also provided a use of a plastic
sheeting for packaging of frozen foods, wherein
the plastic sheeting comprises at least one side with at least one layer which
contains a rough surface to increase a coefficient of friction thereof;
the plastic sheeting and the at least one layer with the rough surface is
produced
by a coextrusion process; and
the at least one layer with the rough surface is formed in the plastic
sheeting by
a dissolved propellant which generates gas bubbles immediately after leaving a
coextrusion nozzle, the gas bubbles despoiling the at least one layer in such
a
way that an irregularly rough surface is produced.
According to the present invention, there is provided a process for producing
a
plastic sheeting with a rough surface to increase the coefficient of friction,
comprising equipping at least one side of the sheeting with at least one layer
which contains the rough surface,
CA 02597766 2007-08-31
2b
equipping at least one side of the sheeting with at least one layer which
contains
the rough surface,
wherein the actual plastic material sheeting and the at least one layer
equipped
with the rough surface is produced by the coextrusion process;
said at least one layer equipped with the rough surface is formed in the
plastic
material by a dissolved propellant which generates gas bubbles immediately
after leaving a coextrusion nozzle, which gas bubbles despoil the at least one
layer in such a way that an irregularly rough surface is produced.
According to the present invention there is also provided a process for
producing
a plastic sheeting with a rough surface to increase the coefficient of
friction,
comprising:
equipping at least one side of the sheeting with a layer which contains the
rough
surface,
wherein at least one of the layers producing the rough surface is applied by
coating; and
wherein the coating consists of a binder and a filler, and the filler is
equipped
with a granular structure.
One advantageous embodiment of the invention lies in the fact that at least
one of
the layers equipped witll the rough surface contains a propellant which
produces
gas bubbles immediately aftei- leaving the coextrusion nozzle, which gas
bubbles
despoil the layer in such a way that an irregularly rough surface is created.
Sucli an embodiment has proved very advantageous.
Accordiii- to a fui-tlie-- embodiment of the invention, it is, however, also
possible
that at least one of the layers producing the rou(.11h surface is applied by
the
coatin~ metliod.
A completely separate embodiment of the layer is also made possible thereby.
A very advantageous fu--thei- embodiment of the invention is chai-actei-ized
in that
the coating material consists of a binder and a filler.
CA 02597766 2008-10-01
3
wherein the actual plastic material sheeting and the at least one layer
equipped
with the rough surface is produced by the coextrusion process;
said at least one layer equipped with the rough surface is formed in the
plastic
material by a dissolved propellant which generates gas bubbles immediately
after leaving a coextrusion nozzle, which gas bubbles despoil the at least one
layer in such a way that an irregularly rough surface is produced.
According to the present invention there is also provided a process for
producing
a plastic sheeting with a rough surface to increase the coefficient of
friction,
comprising:
equipping at least one side of the sheeting with a layer which contains the
rough
surface,
wherein at least one of the layers producing the rough surface is applied by
coating;
wherein the coating consists of a binder and a filler, and the filler is
equipped
with a granular structure; and
wherein the coating is applied by drawing.
One advantageous embodiment of the invention lies in the fact that at least
one of
the layers equipped with the rough surface contains a propellant which
produces
gas bubbles immediately after leaving the coextrusion nozzle, which cas
bubbles
despoil the layei- in such a way that an ii-regularly rough sLu-face is
created.
Such an embodiment has proved veiy advantageous.
According to a fii--ther embodiment of the invention, it is, howevcr, also
possible
that at least one of the layers producing the rough stuTace is applied by the
coating method.
A conipletely separate embodii ent of the layer is also made possible thereby.
A vei-y advantageous fui-ther embodiment of the invention is chai-acterized in
that
the coating material consists of a binder and a filler.
CA 02597766 2008-10-01
4
Fig. 1 shows a plan view of a plastic sheeting which is produced together
with a top layer by the coextrusion process and which is equipped
with largely torn surface.
Fig. 2 shows a plan view of a plastic sheeting with a striated application
of a granular filler
Fig. 3 shows a plan view of a fiirther plastic sheeting with filler in a
ramified form.
The 1 in Fig. I designates a plastic sheeting which consists of a base
sheeting,
not described in greater detail, and a surface layer 2 coextruded with it.
This
surface layer 2 consists of a polyolefine, for example high-density
polyethylene
or polypropylene, in which a propellant is dissolved, which propellant foams
when pressure is released on expulsion of the sheeting from the coexti-usion
nozzle, and tears the surface of the layer. The structure of surface layer 2
shown
in Fig. I is produced thereby.
In the embodiment example shown in Fig. 2, a plastic sheeting 2 1 is provided,
which plastic sheeting contains a base sheeting, also not visible, which base
sheeting is coated with a surface layer 22. This layer 22 consists of a binder
and a
filler 23, which are intimately mixed on application to the base sheeting. On
application, however, a concentration of the filler 23 in interrupted
longitudinal
streaks takes place owing to the drawing-type application.
Conversely, in the case of a differentiated application, a ramified
application
structure 33 is achieved within application layer 32 on plastic sheeting 31.
CA 02597766 2007-08-31
In the two embodiment examples shown in Fig. 2 and 3, the binder can be
applied over the entire surface or just in the area of the filler structnre.
Depending on the intended purpose, corundwn or silica sand is used as the
filler,
being used in a proportion of 20 to 70% of the total application weight.
The application weight is appi-oximately 5 to 50 g/m' and the particle size of
the
filler is 40 to 250 m.
All three embodiments result in a very high coefficient of friction for the
plastic
sheeting, so it can be used in ntunerous ways.
One possible application is in covering roof surfaces, makinb it possible to
walk
on them without a danger of slipping.
It is possible here to cover both purely timber boarding as well as viscous
surfaces with the plastic sheeting.
These plastic sheetings can also be used very effectively for packaging frozen
foods, since the slippage of the normally extremely smooth film packaging is
effectively prevented.
It is also possible to coat the base sheeting on both sides, whei-eby various
embodiments of the surface layers are possible.